thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45MPa未退火	ASTM D648	200 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.80MPa未退火	ASTM D648	110 °C
Linear coefficient of thermal expansion	MD	ASTM D696	4E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD	ASTM D696	4E-05 cm/cm/°C

flame retardant performance	Test Condition	Test Method	Test Result
UL flame retardant rating		UL -94	V-0 0.75mm

Physical properties	Test Condition	Test Method	Test Result
shrinkage rate	MD	ASTM D995	1.30 %
shrinkage rate	shrinkage rate	TD	ASTM D995	1.50 %
Water absorption rate	(23°C,24hr)	ASTM D570	0.02 %

Electrical performance	Test Condition	Test Method	Test Result
volume resistivity		ASTM D257	1E+16 Ω.cm
dielectric strength	1.60mm	ASTM D149	23 KV/mm
dielectric constant	23°C	ASTM D150	3.3 1MHz
Dissipation Factor	23°C	ASTM D150	2E-03 1MHz
	Dissipation Factor	耐电弧性	ASTM D495	125 S
	Dissipation Factor	Dissipation Factor	相对漏电起痕指数	ASTM D3638	135 V

mechanical properties	Test Condition	Test Method	Test Result
coefficient of friction	静态	ASTM D3702	0.35
tensile strength	23°C	ASTM D638	80 Mpa
Elongation at break	23°C	ASTM D638	>15 %
Tensile modulus	23°C	ASTM D638	4200 Mpa
Tensile modulus	Tensile modulus	泊松比		7.58 0.38
bending strength	23°C	ASTM D790	130 Mpa
flexural modulus	23°C	ASTM D790	3800 Mpa
Impact strength of cantilever beam gap	23°C	ASTM D256	40 J/m
coefficient of friction	动态	ASTM D3702	0.40

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.