PP ExxonMobil™ PP3295G1 EXXONMOBIL USA
267
- Unit Price:US$ 1,541 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Dimensional stability｜Easy to color｜High impact
- Application Areas:chip｜Automotive sector｜Seals｜Non-woven fabric｜Industrial applications
- Color:--
- Grade:--
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | 74.48to85.52 MPa | ||
| Rockwell hardness | 23℃ | 84to106 |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| gloss | 46to47 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 1.8MPa, Not annealed | °C | 59to91 | |
| 0.45MPa, Not annealed | °C | 109to133 | |
| 1.8MPa, Not annealed | °C | 58to91 | |
| 0.45MPa, Not annealed | °C | 110to139 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot filament ignition temperature | °C | 548to804 | |
| Burning wire flammability index | °C | 643to960 | |
| Limiting Oxygen Index | % | 21 | |
| burning rate | mm/min | 0.0to101.6 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dart impact | 23℃ | N.m | 26.55to73.89 |
| Impact strength of simply supported beam without notch | 23℃ | kJ/m² | 2.229to8.821 |
| Dart impact | 23℃ | N.m | 8.85to80.35 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt volume flow rate | 230°C/2.16kg | ISO 527-2/5 | 0.01to0.07 |
| 23℃,24hr | % | 0.020to0.052 | |
| Flow: 23 ℃ | 流动,23℃ | mm/mm | 139.7E-3-0.432 |
| 230°C/2.16kg | g/10min | 0.95to20 | |
| Lateral flow: 23 ℃ | 横向, 23℃ | mm/mm | 0.279to0.457 |
| 230°C/2.16kg | g/10min | 4.9to21 | |
| 23℃,24hr | % | 0.030to0.050 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | ohms | 1.0E+14-1.0E+15 | |
| Compared to the Leakage Tracking Index (CTI) | V |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Yield, 23 ℃ | % | 2.6to7.2 | |
| Fracture, 23 ℃ | 44.76to59.03 MPa | ||
| % | 2.0to31 | ||
| Yield, 23 ℃ | 28.41to36.76 MPa | ||
| Fracture, 23 ℃ | 19.03to32.83 MPa | ||
| Yield, 23 ℃ | 51.38to55.59 MPa | ||
| 27.93to35.24 MPa | |||
| Fracture, 23 ℃ | 21.72to30.28 MPa | ||
| Yield, 23 ℃ | % | 1.7to8.4 | |
| Fracture, 23 ℃ | % | 3.7to31 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.