POM DURACON® GH-20 JAPAN POLYPLASTIC
229
- Unit Price:US$ 2,591 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:160.5MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High rigidity｜High hardness｜Low contractility｜Low warpage｜Anti creep｜Filler: Glass fiber reinforced material｜VOC｜20% filler by weight｜20% filler by weight
- Application Areas:Automotive sector｜Industrial machinery｜Engine parts｜bearing｜machine｜Mechanical components
- Color:--
- Grade:Enhanced level
Material Certification
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M级 | ISO 2039-2 | 85 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火 | ISO 75-2/A | 158 °C |
| Linear coefficient of thermal expansion | MD：23到55°C | 内部方法 | 3E-05 cm/cm/°C |
| TD：23to55°C | 内部方法 | 1E-04 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ColorNumber | CF3500 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.2 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.54 g/cm³ | |
| melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 3.0 g/10min |
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 2.30 cm3/10min |
| shrinkage rate | TD:2.00mm | ISO 294-4 | 1.0 % |
| MD:2.00mm | ISO 294-4 | 0.80 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.70 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 7000 Mpa | |
| tensile strength | ISO 527-2 | 100 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 2.0 % |
| flexural modulus | ISO 178 | 6000 Mpa | |
| bending strength | ISO 178 | 135 Mpa | |
| coefficient of friction | Dynamic2 | JISK7218 | 0.42 |
| 与钢-动态3 | JISK7218 | 0.55 | |
| Wear factor | 0.49MPa,0.30m/sec4 | JISK7218 | 200 10^-8mm³/N·m |
| 0.060MPa,0.15m/sec5 | JISK7218 | 300 10^-8mm³/N·m | |
| 0.49MPa,0.30m/sec6 | JISK7218 | 7000 10^-8mm³/N·m | |
| 0.060MPa,0.15m/sec7 | JISK7218 | 10000 10^-8mm³/N·m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.