PEI

PEI ULTEM™ 2312-1000 SABIC INNOVATIVE SHANGHAI

252

Unit Price:US$ 16,289 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
21.1MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High temperature resistance｜enhance
Application Areas:Fitness equipment｜Automotive Applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Reverse notch impact	3.20 mm	ASTM D256	310 J/m

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.8 mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Break, 100 mm Span	ASTM D790	179 Mpa
Bending modulus	100 mm Span	ASTM D790	6550 Mpa
elongation	Break	ASTM D638	3.5 %
tensile strength	Break	ASTM D638	103 Mpa
Tensile modulus		ASTM D638	5990 Mpa

injection	Test Condition	Test Method	Test Result
drying temperature			150 °C
drying time			4.0 to 6.0 hr
Suggested maximum moisture content			0.020 %
Suggested injection volume			40 to 60 %
Temperature at the rear of the barrel			330 to 400 °C
Temperature in the middle of the barrel			340 to 400 °C
Temperature at the front of the material cylinder			345 to 400 °C
Spray nozzle temperature			345 to 400 °C
Processing (melt) temperature			350 to 400 °C
Mold temperature			135 to 165 °C
Back pressure			0.300 to 0.700 Mpa
Screw speed			40 to 70 rpm
Exhaust hole depth			0.025 to 0.076 mm

thermal performance	Test Condition	Test Method	Test Result
RTI		UL 746	170 °C
RTI Imp		UL 746	170 °C
RTI Elec		UL 746	170 °C
Linear coefficient of thermal expansion	Across Flow : -20 to 150°C	ASTM E831	2.7E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow : -20 to 150°C	ASTM E831	2.3E-5 cm/cm/°C
Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	207 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium, 23°C	ASTM D570	0.98 %
Water absorption rate	Water absorption rate	24 hr	ASTM D570	0.18 %
Shrinkage rate	Across FlowFlow : 3.20 mm	Internal Method	0.45 - 0.55 %
Shrinkage rate	Shrinkage rate	Flow : 3.20 mm	Internal Method	0.30 - 0.40 %
melt mass-flow rate	337°C/6.6 kg	ASTM D1238	10 g/10 min

Electrical performance	Test Condition	Test Method	Test Result
Hot wire ignition		UL 746	PLC 1
High voltage arc tracing rate		UL 746	PLC 0
High arc combustion index		UL 746	PLC 3
Compared to the anti leakage trace index		UL 746	PLC 4
Arc resistance		ASTM D495	PLC 7
Dielectric constant	1 MHz	ASTM D150	3.49
Dielectric constant	Dielectric constant	1 kHz	ASTM D150	3.70

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PEI ULTEM™ 2312-1000 SABIC INNOVATIVE SHANGHAI

Material Description

Technical Data Sheet Compare

Technical Data Sheet