PBT VALOX™ DR48-BK1066 SABIC INNOVATIVE SHANGHAI
308
- Unit Price:US$ 3,646 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:60MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜Glass fiber reinforced
- Application Areas:Side track application｜Non specific food｜Lawn equipment｜Garden equipment｜Industrial applications｜Automotive External Parts｜Electrical field｜Electronic field｜Architectural application field｜Outdoor applications｜Electrical appliances｜Engine hood parts｜Medical supplies｜Nursing supplies｜Plastic bag｜Automotive interior parts｜Casters
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Specific volume | ASTM D792 | 0.650 cm³/g | |
| Shrinkage rate | 内部方法 | 0.40 - 0.60 % | |
| 内部方法 | 0.60 - 0.90 % | ||
| 内部方法 | 0.50 - 0.80 % | ||
| 内部方法 | 0.80 - 1.1 % | ||
| Water absorption rate | ASTM D570 | 0.070 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 118 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 | |
| UL 94 | 5VA | ||
| Limiting Oxygen Index | ASTM D2863 | 29 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| tensile strength | ASTM D638 | 93.0 Mpa | |
| Flexural modulus | ASTM D790 | 5200 Mpa | |
| bending strength | ASTM D790 | 140 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ASTM D4812 | 500 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1.0E+15 ohms·cm | |
| dielectric strength | ASTM D149 | 25 KV/mm | |
| ASTM D149 | 19 KV/mm | ||
| dielectric constant | ASTM D150 | 3.60 | |
| ASTM D150 | 3.40 | ||
| Dissipation Factor | ASTM D150 | 2.0E-3 | |
| ASTM D150 | 0.016 | ||
| arc resistance | ASTM D495 | PLC 6 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 3 | |
| High arc combustion index (HAI) | UL 746 | PLC 0 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 4 | |
| Hot wire ignition (HWI) | UL 746 | PLC 3 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 120 °C | ||
| drying time | 3.0 to 4.0 hr | ||
| Suggested maximum moisture content | 0.020 % | ||
| Suggested injection volume | 40 to 80 % | ||
| Temperature at the rear of the barrel | 240 to 255 °C | ||
| Temperature in the middle of the barrel | 245 to 260 °C | ||
| Temperature at the front of the material cylinder | 250 to 265 °C | ||
| Spray nozzle temperature | 245 to 260 °C | ||
| Processing (melt) temperature | 250 to 265 °C | ||
| Temperature | 65 to 90 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| screw speed | 50 to 80 rpm | ||
| Exhaust hole depth | 0.025 to 0.038 mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Hot deformation temperature (HDT) | ASTM D648 | 210 °C | |
| ASTM D648 | 182 °C | ||
| ASTM E831 | 2.0E-5 cm/cm/°C | ||
| ASTM E831 | 2.0E-5 cm/cm/°C | ||
| RTI Elec | UL 746 | 120 °C | |
| RTI Imp | UL 746 | 120 °C | |
| RTI | UL 746 | 140 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.