PBT/PET VALOX™  8032UX BK1A404U SABIC INNOVATIVE US

313
  • Unit Price:US$ 3,260 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    10MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View

For more details, please contact the supplier!

Material Description

  • Material Properties:enhanceFiller: Glass fiber reinforced material30%Filler by weight
  • Application Areas:chipShellHome appliance componentsPhone case
  • Color:--
  • Grade:Injection grade

Technical Data Sheet Compare

physical property Test ConditionTest MethodTest Result
melt mass-flow rateASTM D123815 g/10min
Melt volume flow rateISO 113315.0 cm3/10min
Shrinkage rate内部方法0.40-0.80 %
Shrinkage rate内部方法0.40-0.80 %
Shrinkage rate内部方法0.60-1.0 %
Shrinkage rate内部方法0.60-1.0 %
Water absorption rateISO 620.16 %
Water absorption rateISO 620.050 %
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessISO 2039-2119
ball-indentation hardnessISO 2039-1110 Mpa
flammabilityTest ConditionTest MethodTest Result
UL flame retardant ratingUL 94HB
Mechanical propertiesTest ConditionTest MethodTest Result
--3ASTM D6389950 Mpa
yieldASTM D638115 Mpa
yieldISO 527-2/5145 Mpa
fractureASTM D638115 Mpa
fractureISO 527-2/5145 Mpa
yieldASTM D6382.0 %
yieldISO 527-2/52.4 %
fractureASTM D6382.0 %
fractureISO 527-2/52.5 %
50.0mm spanASTM D7908450 Mpa
--9ISO 1788500 Mpa
--10ISO 178210 Mpa
Yield, 50.0mm spanASTM D790165 Mpa
Taber abraser内部方法30.0 mg
Impact resistanceTest ConditionTest MethodTest Result
Impact strength of simply supported beam without notchISO 179/1eU45 kJ/m²
Charpy Notched Impact StrengthISO 179/1eA9.0 kJ/m²
Charpy Notched Impact StrengthISO 179/1eA9.0 kJ/m²
Impact strength of simply supported beam without notchISO 179/1eU40 kJ/m²
-30°CASTM D25648 J/m
23°CASTM D25657 J/m
-30°CISO 180/1A8.0 kJ/m²
0°CISO 180/1A8.0 kJ/m²
23°CISO 180/1A9.0 kJ/m²
-30°CASTM D4812470 J/m
23°CASTM D4812480 J/m
-30°CISO 180/1U40 kJ/m²
23°CISO 180/1U45 kJ/m²
Dart impactASTM D37638.00 J
Electrical performanceTest ConditionTest MethodTest Result
relative permittivityIEC 602503.60
relative permittivityIEC 602503.20
Dissipation FactorIEC 602508E-04
Dissipation FactorIEC 602508E-04
Dissipation FactorIEC 602500.013
Compared to the Leakage Tracking Index (CTI)UL 746PLC 2
Compared to the Leakage Tracking Index (CTI)IEC 60112PLC 2
Surface ResistivityIEC 60093>1.0E+15 ohms
Volume resistivityIEC 60093>1.0E+15 ohms·cm
dielectric strengthIEC 60243-127 KV/mm
dielectric strengthIEC 60243-123 KV/mm
dielectric strengthIEC 60243-115 KV/mm
relative permittivityIEC 602503.30
relative permittivityIEC 602503.30
Thermal performanceTest ConditionTest MethodTest Result
Flow: 23 to 60 ° CISO 11359-22.2E-05 cm/cm/°C
Horizontal: -40 to 40 ° CASTME8317.5E-05 cm/cm/°C
Horizontal: 23 to 60 ° CISO 11359-28.1E-05 cm/cm/°C
0.45MPa, Unanealed, 3.20mmASTM D648208 °C
0.45MPa, Unanealed, 100mm spanISO 75-2/Be217 °C
1.8MPa, Unanealed, 3.20mmASTM D648190 °C
1.8MPa, Unanealed, 100mm spanISO 75-2/Ae195 °C
ball-indentation hardnessIEC 60695-10-2Pass
Flow: -40 to 40 ° CASTME8312.5E-05 cm/cm/°C
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.