PC/PBT XENOY™  1760-7001 SABIC INNOVATIVE US

330
  • Unit Price:US$ 3,067 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    53MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Chemical resistance｜High mobility｜Glass fiber reinforced｜High impact resistance
  • Application Areas:Automotive External Parts
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Dart impact-30°C, Energy at PeakASTM D37633.00 J
Dart impact-30°C, Total EnergyASTM D37633.00 J
Dart impact-20°C, Energy at PeakASTM D37634.00 J
Dart impact23°C, Total EnergyASTM D37638.00 J
mechanical propertiesTest ConditionTest MethodTest Result
Tensile modulus--1ASTM D6385310 Mpa
Tensile modulus--ISO 527-2/14800 Mpa
tensile strengthYield2ASTM D63884.0 Mpa
tensile strengthYieldISO 527-2/584.0 Mpa
tensile strengthBreak2ASTM D63884.0 Mpa
tensile strengthBreakISO 527-2/584.0 Mpa
elongationYield2ASTM D6383.0 %
elongationYieldISO 527-2/53.0 %
elongationBreak2ASTM D6383.0 %
elongationBreakISO 527-2/53.0 %
Bending modulus50.0 mm Span3ASTM D7903910 Mpa
Bending modulus--4ISO 1784010 Mpa
bending strength--4,5ISO 178133 Mpa
bending strengthYield, 50.0 mm Span3ASTM D790131 Mpa
injectionTest ConditionTest MethodTest Result
drying temperature110 °C
drying time4.0 to 6.0 hr
Suggested maximum moisture content0.020 %
Suggested injection volume50 to 80 %
Temperature at the rear of the barrel250 to 270 °C
Temperature in the middle of the barrel255 to 275 °C
Temperature at the front of the material cylinder260 to 280 °C
Spray nozzle temperature255 to 275 °C
Processing (melt) temperature260 to 280 °C
Mold temperature65 to 95 °C
Back pressure0.300 to 0.600 Mpa
Screw speed50 to 80 rpm
Exhaust hole depth0.013 to 0.020 mm
thermal performanceTest ConditionTest MethodTest Result
Hot deformation temperature1.8 MPa, Unannealed, 3.20 mmASTM D648125 °C
Hot deformation temperature1.8 MPa, Unannealed, 6.40 mmASTM D648116 °C
Hot deformation temperature1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span7ISO 75-2/Af101 °C
Vicat softening temperature--ASTM D15258121 °C
Vicat softening temperature--ISO 306/B50135 °C
Vicat softening temperature--ISO 306/B120130 °C
Linear coefficient of thermal expansionFlow : -40 to 40°CASTM E8313.9E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : -40 to 40°CASTM E8317.6E-5 cm/cm/°C
Linear coefficient of thermal expansionAcross Flow : -40°CISO 11359-27.6E-5 cm/cm/°C
Physical propertiesTest ConditionTest MethodTest Result
melt mass-flow rate250°C/5.0 kgASTM D123815 g/10 min
Melt Volume Flow Rate (MVR)265°C/5.0 kgISO 113327.0 cm3/10min
Shrinkage rateFlow : 3.20 mmInternal Method0.40 - 0.60 %
Shrinkage rateAcross FlowFlow : 3.20 mmInternal Method0.40 - 0.60 %
Water absorption rateSaturation, 23°CISO 620.50 %
Water absorption rateEquilibrium, 23°C, 50% RHISO 620.15 %
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.