PC IUPILON™ GS2010MDR MITSUBISHI ENGINEERING JAPAN

223

Unit Price:US$ 2,552 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
21MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜enhance｜Filler: Glass fiber reinforced material｜10% filler by weight
Application Areas:fibre
Color:--
Grade:Enhanced level

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179	55 kJ/m²

machinability	Test Condition	Test Method	Test Result
Mold temperature			80-120 °C
Screw speed			50-100 rpm
Processing temperature			280-300 °C
	Processing temperature			290-310 °C
	Processing temperature	Processing temperature			270-290 °C
Dry conditions			热风干燥 120℃---約4-8小时

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.75mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ASTM D790/ISO 178	107 kg/cm²(MPa)[Lb/in²]
Bending modulus		ASTM D790/ISO 178	2900 kg/cm²(MPa)[Lb/in²]
Tensile modulus		ASTM D638/ISO 527	3500 kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	4.8 %
bending strength		ISO 178	135 Mpa
Bending modulus		ISO 178	4000 Mpa
Tensile strain	Break	ISO 527-2	2.9 %
tensile strength	Break	ISO 527-2	78.0 Mpa
Tensile modulus		ISO 527-2	4500 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	145 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	140 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	4E-05 cm/cm/°C
	Linear coefficient of thermal expansion	TD	ISO 11359-2	6.7E-05 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion		ASTM D696/ISO 11359	5.0E-05 mm/mm.℃

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	TD:3.20mm		0.40-0.60 %
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	9.00 cm3/10min
melt mass-flow rate	300°C/1.2kg	ISO 1133	10 g/10min
Shrinkage rate		ASTM D955	0.3 - 0.5 %
density		ASTM D792/ISO 1183	1.27
Water absorption rate	Saturation,23°C	ISO 62	0.14 %
Shrinkage rate	MD:3.20mm		0.30-0.50 %

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index	CTI	UL 746	PLC 4

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC IUPILON™ GS2010MDR MITSUBISHI ENGINEERING JAPAN

Material Description

Technical Data Sheet Compare

Technical Data Sheet