Material Properties:enhance｜Conductive｜Filler: Carbon fiber reinforced material｜30%｜Filler by weight
Application Areas:Electrical appliances｜Electronic and Electrical Applications
Color:--
Grade:--

Technical Data Sheet Compare

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	1.8MPa,未退火	ISO 75-2/A	250 °C
melting temperature		DSC	265 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	2E-05 cm/cm/°C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB

Physical properties	Test Condition	Test Method	Test Result
shrinkage rate	TD:3.00mm3	内部方法	0.60 %
	shrinkage rate	MD:3.00mm4	内部方法	0.20 %
	shrinkage rate	shrinkage rate	吸水率(平衡,23°C,50%RH)	内部方法	1.8 %
PVLimit-vs.S45C		SuzukiMethod	2.6 MPa·m/s

Electrical performance	Test Condition	Test Method	Test Result
volume resistivity		IEC 60093	2.0 ohms·cm

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	23°C	ISO 527-2	240 Mpa
Tensile strain	断裂,23°C	ISO 527-2	1.6 %
flexural modulus	23°C	ISO 178	19000 Mpa
bending strength	23°C	ISO 178	335 Mpa
AmountofWear-vs.S45C		SuzukiMethod	0.600 mg/hr
Friction coefficient - vs.S45C		SuzukiMethod	0.23

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.