PA46 Stanyl® TE300 DSM HOLAND

219

Unit Price:US$ 5,874 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
60.5MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:Thermal stability
Application Areas:Electronic and electrical components｜Casters
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet Compare

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	0.45 MPa, 未退火	ISO 75-2/B	280 °C
Heat Deflection Temperature	Heat Deflection Temperature	1.8 MPa, 未退火	ISO 75-2/A	190 °C
melting temperature		ISO 11357-3	295 °C
Linear coefficient of thermal expansion	流动	ISO 11359-2	8.5E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	横向	ISO 11359-2	1.1E-4 cm/cm/°C
RTI Elec	0.9 mm	UL 746	130 °C
Thermal Index - 5000 hr		IEC 60216	128 °C

flammability	Test Condition	Test Method	Test Result
Flammability level		UL 94	V-2
Flammability level	Flammability level		UL 94	V-2

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	4.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	10 kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of cantilever beam gap	-40°C	ISO 180/1A	4.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	10 kJ/m²

Electrical performance	Test Condition	Test Method	Test Result
volume resistivity		IEC 60093	1.0E+15 ohms·cm
dielectric strength		IEC 60243-1	25 KV/mm
relative permittivity	100 Hz	IEC 60250	4.00
relative permittivity	relative permittivity	1 MHz	IEC 60250	3.60
Compared to the Leakage Tracking Index (CTI)		IEC 60112	PLC 0

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	平衡, 23°C, 50% RH	ISO 62	3.7 %
shrinkage rate	流量	ISO 294-4	2.0 %
shrinkage rate	shrinkage rate	横向流量	ISO 294-4	2.0 %
density		ISO 1183	1.18 g/cm³

mechanical properties	Test Condition	Test Method	Test Result
Nominal tensile fracture strain	200°C	ISO 527-2	> 50 %
	Nominal tensile fracture strain	180°C	ISO 527-2	> 50 %
		Nominal tensile fracture strain	160°C	ISO 527-2	> 50 %
		Nominal tensile fracture strain	Nominal tensile fracture strain	120°C	ISO 527-2	> 50 %
tensile strength	屈服, 200°C	ISO 527-2	30.0 Mpa
flexural modulus	--	ISO 178	3000 Mpa
	flexural modulus	120°C	ISO 178	800 Mpa
	flexural modulus	flexural modulus	160°C	ISO 178	600 Mpa
Nominal tensile fracture strain	--	ISO 527-2	40 %
tensile strength	屈服, 180°C	ISO 527-2	35.0 Mpa
	tensile strength	屈服, 160°C	ISO 527-2	40.0 Mpa
		tensile strength	屈服, 120°C	ISO 527-2	50.0 Mpa
		tensile strength	tensile strength	屈服	ISO 527-2	100 Mpa
Tensile modulus	200°C	ISO 527-2	500 Mpa
	Tensile modulus	160°C	ISO 527-2	650 Mpa
		Tensile modulus	180°C	ISO 527-2	600 Mpa
			Tensile modulus	120°C	ISO 527-2	800 Mpa
			Tensile modulus	Tensile modulus	--	ISO 527-2	3300 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.