Material Description

Material Properties:Flame retardant｜Filler: Glass fiber reinforced material｜40%｜Filler by weight
Application Areas:Electronic and electrical components｜Application in the automotive field
Color:--
Grade:Fill level

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23°C	ISO 179/1eA	13	kJ/m²
Impact strength of cantilever beam gap	23°C,3.18mm	ASTM D256	98	J/m
	Impact strength of cantilever beam gap	23°C,6.35mm	ASTM D256	85	J/m
	Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	11	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.9mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Bending modulus		ISO 178	13400	Mpa
bending strength		ASTM D790	265	Mpa
bending strength	bending strength		ISO 178	260	Mpa
Bending modulus		ASTM D790	12700	Mpa
Tensile strain	Break	ISO 527-2/5	2.7	%
elongation	Break	ASTM D638	3.0	%
tensile strength	Break	ISO 527-2/5	180	Mpa
	tensile strength	Break	ASTM D638	177	Mpa
		tensile strength	Yield	ISO 527-2/5	180	Mpa
		tensile strength	tensile strength	Yield	ASTM D638	186	Mpa
Tensile modulus		ISO 527-2/5	11400	Mpa
Tensile modulus	Tensile modulus		ASTM D638	6860	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Annealed,4.00mm	ISO 75-2/A	272	°C
	Hot deformation temperature	1.8MPa,Unannealed,4.00mm	ISO 75-2/A	267	°C
		Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	270	°C
			Hot deformation temperature	0.45MPa,Annealed,4.00mm	ISO 75-2/B	283	°C
				Hot deformation temperature	0.45MPa,Unannealed,4.00mm	ISO 75-2/B	283	°C
				Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,6.40mm	ASTM D648	282	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	316°C/5.0kg	ISO 1133	83	g/10min
melt mass-flow rate	melt mass-flow rate	316°C/5.0kg	ASTM D1238	55	g/10min
density		ISO 1183	1.66	g/cm³
density	density		ASTM D792	1.66	g/cm³
ash content		ASTM D5630	40	%
Shrinkage rate	TD：3.20mm	ASTM D955	0.32-0.39	%
Shrinkage rate	Shrinkage rate	MD：3.20mm	ASTM D955	0.27-0.33	%
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ISO 2039-2	121
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	121

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join