SPS XAREC™ C122 IDEMITSU JAPAN

421

Unit Price:US$ 2,678 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
33MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High temperature resistance｜Glass fiber reinforced
Application Areas:Household daily necessities｜Electrical applications
Color:--
Grade:Injection grade

Material Certification

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179	35 kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180	30 kJ/m²

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.8mm	UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	5400 Mpa
tensile strength	Break	ISO 527-2	75.0 Mpa
Tensile strain	Break	ISO 527-2	2.7 %
Bending modulus		ISO 178	5000 Mpa
bending strength		ISO 178	120 Mpa
Elongation at Break		ASTM D638/ISO 527	2.7 %
tensile strength		ASTM D638/ISO 527	75 kg/cm²(MPa)[Lb/in²]
Rockwell hardness		ASTM D785	45
Bending modulus		ASTM D790/ISO 178	5 kg/cm²(MPa)[Lb/in²]
bending strength		ASTM D790/ISO 178	120 kg/cm²(MPa)[Lb/in²]

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	260 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	140 °C
Linear coefficient of thermal expansion	MD：-30to30°C	TMA	3E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-30to30°C	TMA	8.1E-05 cm/cm/°C
RTI Elec		UL 746	50.0 °C
RTI Imp		UL 746	50.0 °C
RTI Str		UL 746	50.0 °C
Combustibility (rate)		UL 94	HB/0.80
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	MD 3 mm/mm.℃

Physical properties	Test Condition	Test Method	Test Result
Shrinkage rate	TD	Internal Method	0.50-0.80 %
Shrinkage rate	Shrinkage rate	MD	Internal Method	0.40-0.70 %
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.010 %
density		ASTM D792/ISO 1183	1.11
Shrinkage rate		ASTM D955	MD 0.4-0.7 %
Water absorption rate		ASTM D570/ISO 62	0.01 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		IEC 60093	>1.0E+16 ohms·cm
Dielectric strength		ASTM D149	45 KV/mm
Dielectric constant	1MHz	IEC 60250	2.80
Dissipation factor	1MHz	IEC 60250	<1.0E-3
Arc resistance		ASTM D495	PLC6
Compared to the anti leakage trace index	CTI)3	IEC 60112	PLC 0
Arc resistance		ASTM D495/IEC 60112	105
Volume resistivity		ASTM D257/IEC 60093	>1.0*10^16 Ω.cm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.