PC INFINO® EN-1052W FWA096 LOTTE CHEM DONGGUAN

265

Unit Price:US$ 2,169 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.75 mm	UL 94	V-2
	UL flame retardant rating	1.5 mm	UL 94	V-0
	UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	--2	ASTM D638	2000 Mpa
Tensile modulus	Tensile modulus	--	ISO 527-2/50	2000 Mpa
tensile strength	Yield2	ASTM D638	58.0 Mpa
	tensile strength	Yield	ISO 527-2/50	55.0 Mpa
		tensile strength	Break2	ASTM D638	59.0 Mpa
		tensile strength	tensile strength	Break	ISO 527-2/50	60.0 Mpa
elongation	Break2	ASTM D638	100 %
elongation	elongation	Break	ISO 527-2/50	100 %
Bending modulus	--3	ASTM D790	2100 Mpa
Bending modulus	Bending modulus	--4	ISO 178	2100 Mpa
bending strength	--3	ASTM D790	78.0 Mpa
bending strength	bending strength	--4	ISO 178	80.0 Mpa

injection	Test Condition	Test Method	Test Result
Hot air dryer			100 to 120 °C
Vacuum drying machine			100 to 120 °C
Hot air dryer			4.0 hr
Vacuum drying machine			4.0 hr
Suggested maximum moisture content			0.020 %
Temperature at the rear of the barrel			220 to 260 °C
Temperature in the middle of the barrel			240 to 280 °C
Temperature at the front of the material cylinder			260 to 300 °C
Spray nozzle temperature			260 to 300 °C
Mold temperature			70 to 100 °C
Injection pressure			68.6 to 127 Mpa
Back pressure			0.981 to 1.96 Mpa
Screw speed			60 to 90 rpm

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	126 °C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm	ISO 75-2/A	123 °C
Vicat softening temperature		ISO 306/B50	142 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	250°C/10.0 kg	ASTM D1238	30 g/10 min
Shrinkage rate	Flow : 3.20 mm	ASTM D955	0.40 - 0.70 %
	Shrinkage rate	Across FlowFlow : 3.20 mm	ASTM D955	0.40 - 0.70 %
		Shrinkage rate	横向Flow : 2.00 mm	ISO 294-4	0.40 - 0.70 %
		Shrinkage rate	Shrinkage rate	Flow : 2.00 mm	ISO 294-4	0.40 - 0.70 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R-Scale	ASTM D785	118
Rockwell hardness	Rockwell hardness	R -Sale	ISO 2039-2	119

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.