flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.600mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ASTM D638	2560	Mpa
tensile strength	Yield	ASTM D638	59.0	Mpa
tensile strength	tensile strength	Break	ASTM D638	52.0	Mpa
elongation	Yield	ASTM D638	5.7	%
elongation	elongation	Break	ASTM D638	64	%
Bending modulus	50.0mmSpan	ASTM D790	2300	Mpa
bending strength	Yield,50.0mmSpan	ASTM D790	91.0	Mpa
bending strength	bending strength	Break,50.0mmSpan	ASTM D790	90.0	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	124	°C
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	6.3E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	6.9E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
melt mass-flow rate	300°C/1.2kg	ASTM D1238	12	g/10min
Shrinkage rate	MD:24hr	ASTM D955	0.60-0.65	%
Shrinkage rate	Shrinkage rate	TD:24hr	ASTM D955	0.60-0.65	%
Water absorption rate	24hr,50%RH	ASTM D570	0.010	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Relative permittivity	1.00GHz	IEC 60250	2.92
Dissipation factor	1.00GHz	IEC 60250	7E-03

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.