PC/PBT XENOY™ 6620U-1001 SABIC INNOVATIVE SHANGHAI
282
- Unit Price:US$ 2,805 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:135MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Chemical resistance｜Low temperature impact resistance
- Application Areas:Plastic bag｜Lighting applications｜Household daily necessities
- Color:--
- Grade:--
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 9.9E-05 cm/cm/°C |
| MD：-40到40°C | ISO 11359-2 | 9.9E-05 cm/cm/°C | |
| TD：-40到40°C | ASTME831 | 1E-04 cm/cm/°C | |
| TD：-40到40°C | ISO 11359-2 | 1E-04 cm/cm/°C | |
| RTI Elec | UL 746 | 75.0 °C | |
| RTI Imp | UL 746 | 75.0 °C | |
| RTI Str | UL 746 | 75.0 °C | |
| Heat Deflection Temperature | 0.45MPa,未退火,6.40mm | ASTM D648 | 98.9 °C |
| 1.8MPa,未退火,6.40mm | ASTM D648 | 60.0 °C | |
| 1.8MPa,Unannealed,64.0mmSpan | ISO 75-2/Af | 50.5 °C | |
| vicat | ASTM D152510 | 123 °C | |
| -- | ISO 306/B50 | 119 °C | |
| -- | ISO 306/B120 | 122 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 72 kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 51 kJ/m² |
| 23°C | ISO 180/1A | 54 kJ/m² | |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 56.3 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| arc resistance | ASTM D495 | PLC 5 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 0 |
| High arc combustion index (HAI) | HAI | UL 746 | PLC 0 |
| High Voltage Arc Traceability Rate (HVTR) | HVTR | UL 746 | PLC 1 |
| Hot wire ignition (HWI) | HWI | UL 746 | PLC 3 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | MD：3.20mm | 内部方法 | 1.6-1.8 % |
| TD：3.20mm | 内部方法 | 1.6-1.8 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.14 % |
| Specific volume | ASTM D792 | 0.835 cm³/g | |
| melt mass-flow rate | 266°C/5.0kg | ASTM D1238 | 22 g/10min |
| Melt volume flow rate | 265°C/5.0kg | ISO 1133 | 17.1 cm3/10min |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 1780 Mpa | |
| ISO 527-2/1 | 1830 Mpa | ||
| tensile strength | 屈服 | ASTM D638 | 43.7 Mpa |
| 屈服 | ISO 527-2/50 | 41.1 Mpa | |
| 断裂 | ASTM D638 | 32.9 Mpa | |
| 断裂 | ISO 527-2/50 | 31.7 Mpa | |
| elongation | 屈服 | ASTM D638 | 4.2 % |
| Tensile strain | 屈服 | ISO 527-2/50 | 3.9 % |
| elongation | 断裂 | ASTM D638 | 150 % |
| Tensile strain | 断裂 | ISO 527-2/50 | 19 % |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 1780 Mpa |
| ISO 178 | 1700 Mpa | ||
| bending strength | ISO 178 | 60.0 Mpa | |
| 屈服,50.0mm跨距 | ASTM D790 | 63.6 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.