Material Description

Material Properties:High temperature resistance｜High mobility｜Glass fiber reinforced
Application Areas:Automotive interior parts｜Electrical applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	7.0 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	30 kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	30 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	10 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	9.0 kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	30 kJ/m²
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	30 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180/1A	8.0 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Break	ASTM D638	134 Mpa
Tensile modulus		ISO 527-2/1	9600 Mpa
Tensile modulus	Tensile modulus		ASTM D638	9580 Mpa
Taber abraser	1000Cycles,1000g,CS-17Wheel	Internal Method	65.0 mg
bending strength		ISO 178	192 Mpa
Bending modulus		ISO 178	8120 Mpa
tensile strength	Break	ISO 527-2/5	133 Mpa
elongation	Break	ASTM D638	2.4 %
Tensile strain	Break	ISO 527-2/5	2.5 %
Bending modulus	50.0mmSpan	ASTM D790	7760 Mpa

thermal performance	Test Condition	Test Method	Test Result
Vicat softening temperature	--	ISO 306/A50	165 °C
Hot deformation temperature	1.8MPa,Unannealed,100mmSpan	ISO 75-2/Ae	145 °C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	145 °C
	Hot deformation temperature	Hot deformation temperature	0.45MPa,Unannealed,100mmSpan	ISO 75-2/Be	150 °C
Vicat softening temperature	--	ISO 306/B50	154 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	158 °C
Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	3E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	7E-05 cm/cm/°C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.060 %
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.20 %
Shrinkage rate	TD：3.20mm	Internal Method	0.20-0.50 %
Shrinkage rate	Shrinkage rate	MD：3.20mm	Internal Method	0.10-0.30 %
Melt Volume Flow Rate (MVR)	300°C/10.0kg	ISO 1133	30.0 cm3/10min
melt mass-flow rate	300°C/5.0kg	ASTM D1238	9.0 g/10min

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test	H358/30	ISO 2039-1	240 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PPO NORYL™ FE1630PW 73701 SABIC EU

Material Description

Technical Data Sheet Compare

Technical Data Sheet