PA46 Stanyl® 46HF5040 DSM HOLAND
204
- Unit Price:US$ 6,949 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:65.6MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Flame retardant｜High mobility｜Thermal stability
- Application Areas:Automotive Applications｜Home appliance components
- Color:--
- Grade:Flame retardant and high temperature resistant grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45 MPa, 未退火 | ISO 75-2/B | 290 °C |
| 1.8 MPa, 未退火 | ISO 75-2/A | 290 °C | |
| melting temperature | ISO 11357-3 | 295 °C | |
| Linear coefficient of thermal expansion | 流动 | ASTM D696 | 2.0E-5 cm/cm/°C |
| 流动 | ISO 11359-2 | 1.7E-5 cm/cm/°C | |
| 横向 | ASTM D696 | 4.5E-5 cm/cm/°C | |
| 横向 | ISO 11359-2 | 6.5E-5 cm/cm/°C | |
| RTI Elec | 0.35 mm | UL 746 | 130 °C |
| Thermal Index - 5000 hr | IEC 60216 | 163 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flammability level | UL 94 | V-0 | |
| UL 94 | V-0 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 14 kJ/m² |
| 23°C | ISO 179/1eA | 13 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 40 kJ/m² |
| 23°C | ISO 179/1eU | 50 kJ/m² | |
| Impact strength of cantilever beam gap | -40°C | ISO 180/1A | 15 kJ/m² |
| 23°C | ISO 180/1A | 15 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.77 g/cm³ | |
| shrinkage rate | 横向流量 | ISO 294-4 | 0.90 % |
| 流量 | ISO 294-4 | 0.30 % | |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 1.4 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| volume resistivity | IEC 60093 | > 1.0E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 30 KV/mm | |
| relative permittivity | 100 Hz | IEC 60250 | 4.30 |
| 1 MHz | IEC 60250 | 4.00 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | -- | ISO 527-2 | 15000 Mpa |
| 120°C | ISO 527-2 | 9500 Mpa | |
| 160°C | ISO 527-2 | 6500 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 190 Mpa |
| 断裂, 120°C | ISO 527-2 | 100 Mpa | |
| 断裂, 160°C | ISO 527-2 | 85.0 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 1.7 % |
| 断裂, 120°C | ISO 527-2 | 3.0 % | |
| 断裂, 160°C | ISO 527-2 | 3.0 % | |
| flexural modulus | -- | ISO 178 | 13000 Mpa |
| 120°C | ISO 178 | 8500 Mpa | |
| 160°C | ISO 178 | 5500 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.