Impact strength of simply supported beam without notch
23°C
ISO 179/1eU
无断裂
Impact strength of cantilever beam gap
23°C
ISO 8256/1
330 kJ/m²
flammability
Test Condition
Test Method
Test Result
Burning rate
1.00mm
ISO 3795
42 mm/min
elastomer
Test Condition
Test Method
Test Result
tear strength
Flow
ISO 34-1
140 kN/m
mechanical properties
Test Condition
Test Method
Test Result
tensile strength
10%Strain
ISO 527-2
11.9 Mpa
tensile strength
50%Strain
ISO 527-2
19.0 Mpa
Tensile strain
Break
ISO 527-2
>300 %
Nominal tensile fracture strain
ISO 527-2
380 %
Tensile modulus
ISO 527-2
190 Mpa
tensile strength
Break
ISO 527-2
35.0 Mpa
tensile strength
5.0%Strain
ISO 527-2
7.80 Mpa
thermal performance
Test Condition
Test Method
Test Result
Brittle temperature
ISO 974
-54.0 °C
Melting temperature
ISO 11357-3
211 °C
Physical properties
Test Condition
Test Method
Test Result
melt mass-flow rate
240°C/10.0kg
ISO 1133
10 g/10min
Melt Volume Flow Rate (MVR)
240°C/10.0kg
ISO 1133
10.0 cm3/10min
Shrinkage rate
TD
ISO 294-4
2.1 %
Shrinkage rate
MD
ISO 294-4
2.2 %
hardness
Test Condition
Test Method
Test Result
Shore hardness
ShoreD
ISO 868
58
Shore hardness
ShoreD,15Sec
ISO 868
52
Supplementary Information
Test Condition
Test Method
Test Result
Odor
VDA270
3.50
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.