Material Properties:Low warpage｜high strength｜Filler: Glass fiber reinforced material｜30%｜Filler by weight
Application Areas:Home appliance components｜Electrical applications
Color:--
Grade:--

Technical Data Sheet Compare

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	1.8MPa,未退火	ISO 75-2/A	280 °C
Heat Deflection Temperature	Heat Deflection Temperature	0.45MPa,未退火	ISO 75-2/B	300 °C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	V-0

Supplementary Information	Test Condition	Test Method	Test Result
ColorNumber			VF2201/BK210P

Physical properties	Test Condition	Test Method	Test Result
shrinkage rate	TD:1.00mm	内部方法	0.42 %
shrinkage rate	shrinkage rate	MD:1.00mm	内部方法	0.10 %

Electrical performance	Test Condition	Test Method	Test Result
volume resistivity		IEC 60093	3E+16 ohms·cm
dielectric strength	1.00mm	IEC 60243-1	48 KV/mm
dielectric strength	dielectric strength	3.00mm	IEC 60243-1	23 KV/mm
relative permittivity	1kHz	IEC 60250	4.10
relative permittivity	relative permittivity	1MHz	IEC 60250	3.70
Dissipation Factor	1kHz	IEC 60250	0.020
	Dissipation Factor	1MHz	IEC 60250	0.030
	Dissipation Factor	Dissipation Factor	耐电弧性	IEC 60250	127 sec
Compared to the Leakage Tracking Index (CTI)		IEC 60112	V

mechanical properties	Test Condition	Test Method	Test Result
tensile strength		ASTM D638	150 Mpa
elongation	断裂	ASTM D638	1.6 %
flexural modulus		ISO 178	15000 Mpa
bending strength		ISO 178	200 Mpa
Bending Strain		ISO 178	1.8 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.