PC/PBT LNP™ COLORCOMP™ 6370-BK1G425L SABIC INNOVATIVE US

193

Unit Price:US$ 3,014 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
73MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Impact resistant grade

Technical Data Sheet Compare

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	R级	ASTM D785	109

thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	1.8MPa,未退火,3.20mm	ASTM D648	163 °C
	Heat Deflection Temperature	1.8MPa,未退火,6.40mm	ASTM D648	149 °C
	Heat Deflection Temperature	Heat Deflection Temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	155 °C
vicat		ASTM D152512	153 °C
	vicat	--	ISO 306/B50	148 °C
	vicat	vicat	--	ISO 306/B120	150 °C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	2.7E-05 cm/cm/°C
	Linear coefficient of thermal expansion	MD：60to138°C	ASTME831	2E-05 cm/cm/°C
		Linear coefficient of thermal expansion	MD：-40到40°C	ISO 11359-2	2.7E-05 cm/cm/°C
			Linear coefficient of thermal expansion	TD：-40到40°C	ASTME831	1.1E-04 cm/cm/°C
			Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40到40°C	ISO 11359-2	1.1E-04 cm/cm/°C
RTI Elec		UL 746	140 °C
RTI Imp		UL 746	130 °C
RTI Str		UL 746	140 °C
Heat Deflection Temperature	0.45MPa,未退火,6.40mm	ASTM D648	204 °C

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.5mm	UL 94	HB

Impact resistance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	23°C	ISO 179/1eA	9.0 kJ/m²
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	6.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	10 kJ/m²
Dart impact	23°C,EnergyatPeakLoad	ASTM D3763	5.00 J
Dart impact	Dart impact	23°C,TotalEnergy	ASTM D3763	17.0 J

Electrical performance	Test Condition	Test Method	Test Result
volume resistivity		ASTM D257	4.8E+15 ohms·cm
dielectric strength	1.60mm,在油中	ASTM D149	27 KV/mm
dielectric strength	dielectric strength	3.20mm,inAir	ASTM D149	20 KV/mm
dielectric constant	100Hz	ASTM D150	4.00
dielectric constant	dielectric constant	1MHz	ASTM D150	4.00
Dissipation Factor	100Hz	ASTM D150	3E-03
Dissipation Factor	Dissipation Factor	1MHz	ASTM D150	0.020
arc resistance		ASTM D495	PLC 5
Compared to the Leakage Tracking Index (CTI)	CTI	UL 746	PLC 2
High arc combustion index (HAI)	HAI	UL 746	PLC 3
High Voltage Arc Traceability Rate (HVTR)	HVTR	UL 746	PLC 1
Hot wire ignition (HWI)	HWI	UL 746	PLC 1

Physical properties	Test Condition	Test Method	Test Result
Specific volume		ASTM D792	0.700 cm³/g
melt mass-flow rate	250°C/5.0kg	ASTM D1238	24 g/10min
Melt volume flow rate	250°C/5.0kg	ISO 1133	12.0 cm3/10min
Melt volume flow rate	Melt volume flow rate	265°C/5.0kg	ISO 1133	19.0 cm3/10min
shrinkage rate	MD：--2	内部方法	0.30-0.40 %
	shrinkage rate	MD：--3	内部方法	0.40-0.50 %
		shrinkage rate	TD：--2	内部方法	0.40-0.70 %
		shrinkage rate	shrinkage rate	TD：--3	内部方法	0.70-0.90 %
Water absorption rate	24hr	ASTM D570	0.090 %
	Water absorption rate	饱和,23°C	ISO 62	0.50 %
	Water absorption rate	Water absorption rate	平衡,23°C,50%RH	ISO 62	0.15 %

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	断裂	ISO 527-2/5	3.00 Mpa
Tensile strain	Yield	ASTM D638	3.0 %
	Tensile strain	屈服	ISO 527-2/5	3.0 %
		Tensile strain	Break	ASTM D638	4.0 %
		Tensile strain	Tensile strain	断裂	ISO 527-2/5	110 %
flexural modulus	50.0mm跨距	ASTM D790	5380 Mpa
flexural modulus	flexural modulus		ISO 178	7750 Mpa
bending strength		ISO 178	154 Mpa
	bending strength	屈服,50.0mm跨距	ASTM D790	150 Mpa
	bending strength	bending strength	Break,50.0mmSpan	ASTM D790	138 Mpa
Tensile modulus		ASTM D638	9750 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	8500 Mpa
tensile strength	屈服	ASTM D638	97.0 Mpa
	tensile strength	屈服	ISO 527-2/5	105 Mpa
	tensile strength	tensile strength	Break	ASTM D638	91.0 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.