Material Properties:Low temperature resistance｜High mobility
Application Areas:Automotive components｜Electronic and electrical accessories｜Good molding function
Color:--
Grade:Injection grade

Technical Data Sheet

Basic Performance	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	，Across Flow: 24 hr	ISO 294-4	0.22	%
Water absorption rate		ASTM D570	0.0100	%
density		ASTM D792A	1.58
Shrinkage rate	，Flow: 24 hr	ASTM D955	0.10	%
	Shrinkage rate	，Flow: 24 hr	ISO 294-4	0.18	%
	Shrinkage rate	Shrinkage rate	，Across Flow: 24 hr	ISO 294-4	0.20	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ASTM D638	17500	Mpa
Tensile modulus	Tensile modulus		ISO 527-2	18400	Mpa
tensile strength		ASTM D638	254	Mpa
tensile strength	tensile strength		ISO 527-2	256	Mpa
Elongation at Break		ASTM D638	1.9	%
bending strength	，-	ASTM D790	372	Mpa
bending strength	bending strength	，-	ISO 178	371	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa Unannealed	ISO 75-2/B	258	°C
	Hot deformation temperature	1.8MPa Unannealed	ASTM D648	241	°C
	Hot deformation temperature	Hot deformation temperature	1.8MPa Unannealed	ISO 75-2/A	253	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Impact strength of cantilever beam gap	3.18 mm	ASTM D256	384	J/m

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.