Material Description

Material Properties:Glass fiber reinforced｜Flame retardant
Application Areas:Electrical field｜Electronic field｜Electrical appliances
Color:--
Grade:Injection grade

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ASTM D790	250 Mpa
Bending modulus		ASTM D790	14000 Mpa
elongation	Break	ASTM D638	3.0 %
tensile strength		ASTM D638	160 Mpa

injection	Test Condition	Test Method	Test Result
Temperature at the front of the material cylinder			320 to 335 °C
Spray nozzle temperature			315 to 335 °C
Mold temperature			90 to 140 °C
Injection speed			中等
Screw speed			150 rpm
Temperature in the middle of the barrel			315 to 335 °C
Temperature at the rear of the barrel			300 to 325 °C
Hopper temperature			50 to 90 °C
drying time			2.0 to 6.0 hr
drying temperature			110 °C

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	Across Flow	ASTM D696	5.5E-5 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Flow	ASTM D696	2.5E-5 cm/cm/°C
Melting temperature			310 °C
Glass transition temperature		DSC	85.0 °C
Hot deformation temperature	1.8 MPa, Unannealed	ASTM D648	290 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	24 hr, 100°C	ASTM D570	2.8 %
Water absorption rate	Water absorption rate	24 hr, 23°C	ASTM D570	0.20 %
Shrinkage rate	Across FlowFlow : 2.00 mm	ASTM D955	0.70 %
Shrinkage rate	Shrinkage rate	Flow : 2.00 mm	ASTM D955	0.30 %

Electrical performance	Test Condition	Test Method	Test Result
Dissipation factor	1 MHz	ASTM D150	0.011
Dielectric constant	1 MHz	ASTM D150	4.30
Dielectric strength		ASTM D149	22 KV/mm
Volume resistivity		ASTM D257	1.0E+15 ohms·cm

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M-Scale	ASTM D785	95

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA6T ARLEN™ CH245NK MITSUI CHEM JAPAN

Material Description

Technical Data Sheet Compare

Technical Data Sheet