Material Properties:high strength｜High hardness｜High impact resistance｜High temperature resistance｜wear resistant｜Smoothness｜Chemical resistance
Application Areas:Automotive sector｜Industrial applications｜Electrical field｜Electronic field｜Industrial machinery
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	55	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	90	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
Flammability level		UL 94	HB
ISO Type		ISO 1874	PA 66. MHR. 14-100N. GF 30
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Tensile modulus		ISO 527-2	10000	Mpa
tensile strength	Break	ISO 527-2	200	Mpa
Tensile strain	Break	ISO 527-2	3.5	%
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	250	°C
Hot deformation temperature	Hot deformation temperature	8.0 MPa, Unannealed	ISO 75-2/C	220	°C
Continuous use temperature	--2	ISO 2578	90.0 to 120	°C
Continuous use temperature	Continuous use temperature	--3	Internal Method	200	°C
Melting temperature		ISO 11357-3	260	°C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	2.0E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	1.0E-4	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	横向Flow	ISO 294-4	0.70	%
Shrinkage rate	Shrinkage rate	Flow	ISO 294-4	0.10	%
Water absorption rate	Saturation, 23°C	ISO 62	5.0	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	1.5	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	--	ohms
Volume resistivity		IEC 60093	1.0E+14	ohms·cm
Dielectric strength		IEC 60243-1	38	KV/mm
Compared to the anti leakage trace index		IEC 60112	PLC 1
hardness	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test		ISO 2039-1	230	Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.