Material Description

Material Properties:High mobility｜High impact resistance
Application Areas:Electrical applications｜Automotive interior parts｜Application in the automotive field
Color:--
Grade:Electroplating grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	3030	kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	55.0	J
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	无断裂无断裂
Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	无断裂无断裂
23°C		ISO 180/1A	6060	kJ/m²
-30°C		ISO 180/1A	3030	kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	6060	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂无断裂
-30°C		ASTM D256	400	J/m
23°C		ASTM D256	600	J/m
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
--8		ISO 178	65.0	Mpa
Yield, 50.0mm span		ASTM D790	70.0	Mpa
--7		ISO 178	2000	Mpa
50.0mm span		ASTM D790	2000	Mpa
crack		ISO 527-2/50	100	%
crack	crack		ASTM D638	100	%
yield		ISO 527-2/50	4.0	%
yield	yield		ASTM D638	4.0	%
crack		ISO 527-2/50	40.0	Mpa
crack	crack		ASTM D638	40.0	Mpa
yield		ISO 527-2/50	45.0	Mpa
yield	yield		ASTM D638	45.0	Mpa
--1		ASTM D638	2100	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Ball Pressure Test	75°C	IEC 60695-10-2	Pass
1.8MPa, unannealed, 64.0mm span of		ISO 75-2/Af	92.0	°C
1.8MPa, unannealed, 3.20mm		ASTM D648	90.0	°C
Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	9E-05	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	9E-05	cm/cm/°C
thermal conductivity		ISO 8302	0.20	W/m/K
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.10	%
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.30	%
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70	%
Melt Volume Flow Rate (MVR)	260°C/5.0kg	ISO 1133	13.0	cm3/10min
melt mass-flow rate	260°C/5.0kg	ASTM D1238	14	g/10min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	>1.0E+15	ohms
Volume resistivity		IEC 60093	>1.0E+15	ohms·cm
Dielectric strength	0.800mm,in Oil	IEC 60243-1	35	KV/mm
	Dielectric strength	1.60mm,in Oil	IEC 60243-1	25	KV/mm
	Dielectric strength	Dielectric strength	3.20mm,in Oil	IEC 60243-1	17	KV/mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PC/ABS CYCOLAC™ CP8320-100 SABIC INNOVATIVE US

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index