PA6 Durethan®  BKV30H2.0 BK LANXESS GERMANY

448
  • Unit Price:US$ 2,649 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    53MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Glass fiber reinforcedThermal stability
  • Application Areas:--
  • Color:--
  • Grade:Injection grade

Material Certification

UL

Technical Data Sheet

impact performanceTest ConditionTest MethodTest Result
Suspended wall beam without notch impact strength23°CISO 180/1U60 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU55 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU65 kJ/m²
Suspended wall beam without notch impact strength-30°CISO 180/1U55 kJ/m²
flammabilityTest ConditionTest MethodTest Result
BurningBehaviorISO 3795passed
mechanical propertiesTest ConditionTest MethodTest Result
Bending modulus23°CASTM D7908000 Mpa
Bending modulus23°CISO 178/A8400 Mpa
Tensile strainBreak,23°CISO 527-2/53.0 %
tensile strengthBreak,23°CASTM D638165 Mpa
Tensile modulus23°CISO 527-2/19400 Mpa
Tensile modulus23°CASTM D6388730 Mpa
elongationBreak,23°CASTM D6383.2 %
tensile strengthBreak,23°CISO 527-2/5170 Mpa
bending strength23°CASTM D790260 Mpa
bending strength3.5%StrainISO 178/A255 Mpa
bending strength23°CISO 178260 Mpa
bending strengthFlexuralStrainatFlexuralStrength5(23°C)3.6 %
thermal performanceTest ConditionTest MethodTest Result
Ball Pressure Test210°CIEC 60695-10-2Pass
Vicat softening temperatureISO 306/B120210 °C
Hot deformation temperature8.0MPa,UnannealedISO 75-2/C150 °C
Hot deformation temperature1.8MPa,UnannealedISO 75-2/A210 °C
Hot deformation temperature0.45MPa,UnannealedISO 75-2/B219 °C
Linear coefficient of thermal expansionTD:23to55°CISO 11359-21E-04 cm/cm/°C
Linear coefficient of thermal expansionMD:23to55°CISO 11359-22E-05 cm/cm/°C
Melting temperatureISO 11357-3221 °C
Physical propertiesTest ConditionTest MethodTest Result
Water absorption rateEquilibrium,23°C,50%RHISO 622.1 %
Water absorption rateSaturation,23°CISO 627.0 %
Shrinkage rateMD:120°C,2hr,2.00mm3ISO 294-40.050 %
Shrinkage rateMD:280°C,2.00mm2ISO 294-40.29 %
Shrinkage rateTD:120°C,2hr,2.00mm3ISO 294-40.10 %
Shrinkage rateTD:280°C,2.00mm2ISO 294-40.81 %
Apparent densityISO 600.60 g/cm³
Electrical performanceTest ConditionTest MethodTest Result
Dielectric strength23°C,1.00mmIEC 60243-133 KV/mm
Compared to the anti leakage trace indexSolutionAIEC 60112PLC 1
hardnessTest ConditionTest MethodTest Result
Ball Pressure TestISO 2039-1193 Mpa
filmTest ConditionTest MethodTest Result
Thin film puncture strength--6ISO 6603-22.10 J
Thin film puncture strength--7ISO 6603-22.20 J
Thin film puncture strength--6ISO 6603-2744 N
Thin film puncture strength--7ISO 6603-2803 N
Supplementary InformationTest ConditionTest MethodTest Result
ISO ShortcutISO 1874PA6.GHR.10-090.GF30
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.