Material Description

Material Properties:UV resistance｜Thermal stability
Application Areas:Automotive Applications｜Electrical applications
Color:--
Grade:Extrusion grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	-40°C	ISO 180/1A	NoBreak
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	NoBreak
Charpy Notched Impact Strength	-40°C	ISO 179/1eA	NoBreak
	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	NoBreak
	Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	NoBreak
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	NoBreak

flammability	Test Condition	Test Method	Test Result
Burning rate	1.00mm	ISO 3795	<100 mm/min
UL flame retardant rating	1.5mm	UL 94	HB
	UL flame retardant rating	3.0mm	UL 94	HB
		UL flame retardant rating	1.5mm	IEC 60695-11-10,-20	HB
		UL flame retardant rating	UL flame retardant rating	3.0mm	IEC 60695-11-10,-20	HB
Extreme Oxygen Index		ISO 4589-2	20 %
FMVSS flammability		FMVSS302	B

elastomer	Test Condition	Test Method	Test Result
tear strength	横向Flow	ISO 34-1	120 kN/m
tear strength	tear strength	Flow	ISO 34-1	120 kN/m

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2	85.0 Mpa
tensile strength	Break	ISO 527-2	34.0 Mpa
	tensile strength	10%Strain	ISO 527-2	5.70 Mpa
		tensile strength	50%Strain	ISO 527-2	9.80 Mpa
			tensile strength	100%Strain	ISO 527-2	11.0 Mpa
			tensile strength	tensile strength	300%Strain	ISO 527-2	17.0 Mpa
Tensile strain	Break	ISO 527-2	>300 %
Nominal tensile fracture strain		ISO 527-2	740 %
Bending modulus		ISO 178	87.0 Mpa
Wear resistance		ISO 4649	130 mm³

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	50.0 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	35.0 °C
Brittle temperature		ISO 974	-100 °C
Glass transition temperature		ISO 11357-2	-45.0 °C
Vicat softening temperature	--	ISO 306/A50	155 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	60.0 °C
Melting temperature		ISO 11357-3	193 °C
Linear coefficient of thermal expansion	MD：--	ISO 11359-2	1.7E-04 cm/cm/°C
	Linear coefficient of thermal expansion	MD：-40to23°C	ISO 11359-2	2.2E-04 cm/cm/°C
		Linear coefficient of thermal expansion	TD：--	ISO 11359-2	1.9E-04 cm/cm/°C
			Linear coefficient of thermal expansion	TD：-40to23°C	ISO 11359-2	2.1E-04 cm/cm/°C
			Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：EffectiveThermalDiffusivity	ISO 11359-2	5.44E-08 m²/s

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	1.14 g/cm³
melt mass-flow rate	220°C/2.16kg	ISO 1133	8.5 g/10min
Melt Volume Flow Rate (MVR)	220°C/2.16kg	ISO 1133	7.50 cm3/10min
Shrinkage rate	TD	ISO 294-4	1.1 %
Shrinkage rate	Shrinkage rate	MD	ISO 294-4	1.1 %
Water absorption rate	23°C,24hr	ISO 62	0.60 %
	Water absorption rate	Saturation,23°C,2.00mm	ISO 62	0.60 %
	Water absorption rate	Water absorption rate	Equilibrium,23°C,2.00mm,50%RH	ISO 62	0.20 %

Electrical performance	Test Condition	Test Method	Test Result
Relative permittivity	1MHz	IEC 60250	4.50
Dissipation factor	100Hz	IEC 60250	9.5E-03
Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.030
Compared to the anti leakage trace index		IEC 60112	PLC 0
Surface resistivity		IEC 60093	4E+14 ohms
Volume resistivity		IEC 60093	8E+12 ohms·cm
Dielectric strength		IEC 60243-1	19 KV/mm
Relative permittivity	100Hz	IEC 60250	4.80

hardness	Test Condition	Test Method	Test Result
Shore hardness	ShoreD	ISO 868	45
Shore hardness	Shore hardness	ShoreD,15Sec	ISO 868	42

film	Test Condition	Test Method	Test Result
Water vapor permeability	23°C,85%RH,25μm	DIS15106-1/-2	600 g/m²/24hr

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

TPEE Hytrel® 4556 DUPONT USA

Material Description

Technical Data Sheet Compare

Technical Data Sheet