POM Delrin® 300TE NC010 DUPONT USA
189
- Unit Price:US$ 3,333 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:123.8MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:lubrication
- Application Areas:Automotive components｜household electrical appliances
- Color:--
- Grade:--
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M计秤 | ISO 2039-2 | 69 |
| R计秤 | ISO 2039-2 | 116 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.2E-04 cm/cm/°C |
| TD | ISO 11359-2 | 1.3E-04 cm/cm/°C | |
| AnnealingTemperature | 160 °C | ||
| AnnealingTime-Optional | 30.0 min/mm | ||
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 132 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 71.0 °C | |
| melting temperature | ISO 11357-3 | 178 °C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| burning rate | 1.00mm | ISO 3795 | 46 mm/min |
| FMVSS flammability | FMVSS302 | B |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Emission | VDA275 | <2.00 mg/kg |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 250 kJ/m² |
| 23°C | ISO 179/1eU | NoBreak |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| MediumDensity | 1.15 g/cm³ | ||
| Ejection Temperature | 115 °C | ||
| SpecificHeatCapacity of Melt | 2880 J/kg/°C | ||
| ThermalConductivityofMelt | 0.21 W/m/K | ||
| melt mass-flow rate | ISO 1133 | 6.0 g/10min | |
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 5.80 cm3/10min |
| shrinkage rate | TD | ISO 294-4 | 1.5 % |
| MD | ISO 294-4 | 1.4 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | 3.5%应变 | ISO 178 | 56.0 Mpa |
| Tensile modulus | ISO 527-2 | 2000 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 54.0 Mpa |
| Tensile strain | 屈服 | ISO 527-2 | 20 % |
| Nominal tensile fracture strain | ISO 527-2 | >50 % | |
| flexural modulus | ISO 178 | 1900 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.