PC LEXAN™ LUX9616G WH8A492X SABIC INNOVATIVE NANSHA

232

Unit Price:US$ 4,435 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10.8MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜transparent｜optical performance ｜Thermal stability
Application Areas:Lighting applications
Color:--
Grade:Light diffusion level

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
23°C		ASTM D256	150 J/m
23°C	23°C		ISO 180/1A	15 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	70.0 J

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	1.50mm	UL 94	V-0
Burning wire flammability index	1.00mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	1.00mm	IEC 60695-2-13	850 °C
Hot filament ignition temperature	Hot filament ignition temperature	1.50mm	IEC 60695-2-13	850 °C

mechanical properties	Test Condition	Test Method	Test Result
Yield, 50.0mm span		ASTM D790	95.0 Mpa
crack		ISO 527-2/50	75 %
crack	crack		ASTM D638	80 %
yield		ISO 527-2/50	6.0 %
yield	yield		ASTM D638	6.0 %
crack		ISO 527-2/50	58.0 Mpa
crack	crack		ASTM D638	65.0 Mpa
yield		ISO 527-2/50	62.0 Mpa
yield	yield		ASTM D638	62.0 Mpa
--1		ASTM D638	2300 Mpa
--8		ISO 178	95.0 Mpa
--7		ISO 178	2250 Mpa
50.0mm span		ASTM D790	2160 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD:-40to40°C	ASTME831	6.7E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD:-40to40°C	ASTME831	6.8E-05 cm/cm/°C
Ball Pressure Test	125°C	IEC 60695-10-2	Pass
Vicat softening temperature		ASTM D152513	141 °C
0.45MPa, unannealed, 64.0mm span		ISO 75-2/Bf	135 °C
1.8MPa, unannealed, 3.20mm		ASTM D648	125 °C
1.8MPa, unannealed, 64.0mm span of		ISO 75-2/Af	125 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.15 %
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	0.35 %
Shrinkage rate	MD：3.20mm	Internal Method	0.60-0.80 %
melt mass-flow rate	300°C/1.2kg	ASTM D1238	7.0 g/10min

Electrical performance	Test Condition	Test Method	Test Result
Hot wire ignition	HWI	UL 746	PLC 3
High arc combustion index	HAI	UL 746	PLC 1
Compared to the anti leakage trace index	CTI	UL 746	PLC 3

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.