PC/PBT XENOY™ XL1562 SABIC INNOVATIVE US
206
- Unit Price:US$ 3,195 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:108MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High heat resistance
- Application Areas:Automotive components｜Electronic and electrical components
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | H358/30 | ISO 2039-1 | 100 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD:23到80°C | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| TD:23到80°C | ISO 11359-2 | 1.1E-04 cm/cm/°C | |
| thermal conductivity | ISO 8302 | 0.18 W/m/K | |
| 0.45MPa, Unanealed, 100mm span | ISO 75-2/Be | 110 °C | |
| 1.8MPa, Unanealed, 100mm span | ISO 75-2/Ae | 80.0 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 1.50mm | UL 94 | HB |
| 3.00mm | UL 94 | HB | |
| Burning wire flammability index | 3.20mm | IEC 60695-2-12 | 750 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 18 kJ/m² |
| 23°C | ISO 180/1A | 45 kJ/m² | |
| Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | 无断裂 |
| 23°C | ISO 180/1U | 无断裂 | |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 20 kJ/m² |
| 23°C | ISO 179/1eA | 50 kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| 23°C | ISO 179/1eU | 无断裂 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| volume resistivity | IEC 60093 | >1.0E+14 ohms·cm | |
| dielectric strength | 0.800mm,在油中 | IEC 60243-1 | 32 KV/mm |
| 1.60mm,在油中 | IEC 60243-1 | 25 KV/mm | |
| 3.20mm,在油中 | IEC 60243-1 | 17 KV/mm | |
| relative permittivity | 50Hz | IEC 60250 | 2.80 |
| 60Hz | IEC 60250 | 2.80 | |
| 1MHz | IEC 60250 | 2.90 | |
| Dissipation Factor | 50Hz | IEC 60250 | 2E-03 |
| 60Hz | IEC 60250 | 2E-03 | |
| 1MHz | IEC 60250 | 0.020 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt volume flow rate | 250°C/2.16kg | ISO 1133 | 9.00 cm3/10min |
| 250°C/5.0kg | ISO 1133 | 27.0 cm3/10min | |
| shrinkage rate | MD | 内部方法 | 0.80-1.1 % |
| TD | 内部方法 | 0.80-1.1 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.50 % |
| 平衡,23°C,50%RH | ISO 62 | 0.15 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 2100 Mpa | |
| tensile strength | 屈服 | ISO 527-2/50 | 54.0 Mpa |
| 断裂 | ISO 527-2/50 | 42.0 Mpa | |
| Tensile strain | 屈服 | ISO 527-2/50 | 5.0 % |
| 断裂 | ISO 527-2/50 | 100 % | |
| flexural modulus | ISO 178 | 2000 Mpa | |
| bending strength | ISO 178 | 74.0 Mpa | |
| Taber abraser | 1000Cycles,1000g,CS-17转轮 | 内部方法 | 30.0 mg |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.