PC/PBT

PC/PBT XENOY™ X4820 BK1006 SABIC INNOVATIVE SHANGHAI

289

Unit Price:US$ 3,058 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
107MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility｜High impact resistance｜Dimensional stability
Application Areas:Automotive Applications
Color:--
Grade:Injection grade

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Dart impact	23°C,TotalEnergy	ASTM D3763	60.0 J
Impact strength of cantilever beam gap	23°C	ISO 180/1A	55 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	15 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	60 kJ/m²

mechanical properties	Test Condition	Test Method	Test Result
elongation	Yield	ASTM D638	4.2 %
tensile strength	Break	ISO 527-2/50	52.0 Mpa
	tensile strength	Break	ASTM D638	58.0 Mpa
	tensile strength	tensile strength	Yield	ISO 527-2/50	58.0 Mpa
bending strength	Yield,50.0mmSpan	ASTM D790	91.0 Mpa
bending strength	bending strength		ISO 178	87.0 Mpa
Bending modulus		ISO 178	2850 Mpa
Bending modulus	Bending modulus	50.0mmSpan	ASTM D790	2900 Mpa
Tensile strain	Break	ISO 527-2/50	100 %
elongation	Break	ASTM D638	140 %
Tensile strain	Yield	ISO 527-2/50	4.2 %
Tensile modulus		ASTM D638	3200 Mpa
Tensile modulus	Tensile modulus		ISO 527-2/1	3000 Mpa
tensile strength	Yield	ASTM D638	57.0 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	TD：-40to40°C	ISO 11359-2	1.1E-04 cm/cm/°C
	Linear coefficient of thermal expansion	TD：-40to40°C	ASTME831	1.1E-04 cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：-40to40°C	ISO 11359-2	7.5E-05 cm/cm/°C
Vicat softening temperature		ASTM D152510	130 °C
Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan	ISO 75-2/Af	94.0 °C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	98.0 °C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	7.5E-05 cm/cm/°C
Vicat softening temperature	--	ISO 306/B120	134 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	132 °C

Physical properties	Test Condition	Test Method	Test Result
melt mass-flow rate	250°C/5.0kg	ASTM D1238	10 g/10min
Melt Volume Flow Rate (MVR)	265°C/5.0kg	ISO 1133	12.0 cm3/10min
Shrinkage rate	MD：3.20mm	Internal Method	0.95-1.1 %
Water absorption rate	Saturation,23°C	ISO 62	0.42 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.14 %

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC/PBT XENOY™ X4820 BK1006 SABIC INNOVATIVE SHANGHAI

Material Description

Technical Data Sheet Compare

Technical Data Sheet