PA6

PA6 Ultramid® B3EG6 BASF MALAYSIA

232

Unit Price:US$ 2,317 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Oil resistant｜Filler: Glass fiber reinforced material｜30% filler by weight｜30% filler by weight
Application Areas:Electronic insulation｜Industrial applications｜Industrial applications｜Electronic insulation
Color:--
Grade:Injection grade

Technical Data Sheet

mechanical properties	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	23°C	ISO 180/1A	10 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	8.4 kJ/m²
tensile strength	23°C	ISO 527-2	180 Mpa
Elongation at Break	23°C	ISO 527-2	3.0 %
Tensile modulus	23°C	ISO 527-2	9500 Mpa
Bending modulus	23°C	ISO 178	8600 Mpa
Charpy Notched Impact Strength	23°C	ISO 179/1eA	10 kJ/m²

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	0.45MPaUnannealed	ISO 75-2/Bf	220 °C
Hot deformation temperature	Hot deformation temperature	1.80MPaAnnealed	ISO 75-2/Af	210 °C
Vicat softening temperature	Melting Temperature	ISO 11357-3	220 °C

Physical properties	Test Condition	Test Method	Test Result
density		ISO 1183	1.36 g/cm³
Water absorption rate	(23°C,24hr)	ISO 62	6.00 %
Water absorption rate	Water absorption rate	(23°C,50RH)	ISO 62	2.10 %

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		IEC 60093	1E+13 Ω.cm
Dielectric constant	23°C	IEC 60250	3.80 1MHz
Dissipation factor	23°C	IEC 60250	0.025 100HZ
	Dissipation factor	23°C	IEC 60250	0.025 1MHz
	Dissipation factor	Dissipation factor	相对漏电起痕指数	IEC 60112	550 V

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test		ISO 2039-1	181 Mpa

flame retardant performance	Test Condition	Test Method	Test Result
UL flame retardant rating		UL -94	HB 1.50mm
	UL flame retardant rating		UL -94	HB 2.00mm
	UL flame retardant rating	UL flame retardant rating		UL -94	HB 3.00mm
Ignition temperature of heating wire	1.00mm	IEC 60695-2-12	750 °C
	Ignition temperature of heating wire	2.00mm	IEC 60695-2-12	800 °C
	Ignition temperature of heating wire	Ignition temperature of heating wire	3.00mm	IEC 60695-2-12	750 °C
Relative temperature of heating wire	1.00mm	IEC 60695-2-13	725 °C
	Relative temperature of heating wire	2.00mm	IEC 60695-2-13	775 °C
	Relative temperature of heating wire	Relative temperature of heating wire	3.00mm	IEC 60695-2-13	725 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PA6 Ultramid® B3EG6 BASF MALAYSIA

Material Description

Technical Data Sheet Compare

Technical Data Sheet