PC CH8105 1002 B CANGZHOU DAHUA

Unit Price:US$ 2,420 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
Tianjin port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Transaction Guarantee:

Supplier Information

Dongguan Junkun Plastic Co., Ltd

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:--

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
Refractive index		ISO 489	1.586
Cleanliness	2000?	ISO 14782	0.8	%
transmissivity		ISO 13468	89	%
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Charpy Notched Impact Strength	23℃	ISO 179	NB	kJ/㎡
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23℃	ISO 179	75	kJ/㎡
Suspended wall beam without notch impact strength	23℃	ISO 180	NB	kJ/㎡
Impact strength of cantilever beam gap	23℃	ISO 180	70	kJ/㎡
Bending modulus	2.0mm/min	ISO 178	2410	Mpa
bending strength	Yield2.0mm/min	ISO 178	97	Mpa
elongation	Break50mm/mi	ISO 527	150	%
elongation	elongation	Yield50mm/min	ISO 527	6	%
tensile strength	Yield50mm/min	ISO 527	60	Mpa
Tensile modulus	1.0mm/min	ISO 527	2400	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Glass transition temperature	10℃/min	ISO 11357	149	°C
Vicat softening temperature	50℃/hr 50N	ISO 306	149	°C
Hot deformation temperature	Unannealed1.8MPa	ISO 75	128	°C
Hot deformation temperature	Hot deformation temperature	Annealed0.45MPa	ISO 75	144	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.2	g/cm³
Shrinkage rate	Flow2.0mm	ISO 294	0.50-0.70	%
Shrinkage rate	Shrinkage rate	垂直2.0mm	ISO 294	0.50-0.70	%
melt mass-flow rate	300°C 1.2kg	ISO 1133	10	g/10min
Water absorption rate	23℃ 50RH	ISO 62	0.15	%
Water absorption rate	Water absorption rate	23°C24hr	ISO 62	0.32	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Dielectric constant	100Hz	IEC 60250	3.1
Dielectric strength	1.0mm	IEC 60243	34	KV/mm
Surface resistivity	2.0mm	IEC 60093	10000000000000000	Ω
Volume resistivity	2.0mm	IEC 60093	200000000000000000	Ω.cm
Dielectric constant	1MHz	IEC 60250	3
Dissipation factor	100Hz	IEC 60250	0.001
Dissipation factor	Dissipation factor	1MHz	IEC 60250	0.01
Anti leakage trace index		IEC 60112	250	V
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness		ISO 2039	120
flame retardant performance	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	3.0mm	UL 94	HB
Ignition temperature of heating wire	1.5mm	IEC 60695	875	°C
Ignition temperature of heating wire	Ignition temperature of heating wire	3mm	IEC 60695	875	°C
Relative temperature of heating wire	1.5mm	IEC 60695	875	°C
Relative temperature of heating wire	Relative temperature of heating wire	3mm	IEC 60695	960	°C
Extreme Oxygen Index		ISO 4589	27	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
ASIAPLAS	US$ 2420 /MT

Supplier Join

Get App

Top

PC CH8105 1002 B CANGZHOU DAHUA

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index