POM Delrin® 500PE BK602 DUPONT USA
231
- Unit Price:US$ 3,332 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:111.5MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High rigidity｜Aging resistance｜currency｜Weather resistance
- Application Areas:Automotive sector｜Fitness equipment
- Color:--
- Grade:--
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | M计秤 | ISO 2039-2 | 93 |
| R计秤 | ISO 2039-2 | 121 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 159 °C |
| 1.8MPa,未退火 | ISO 75-2/A | 103 °C | |
| melting temperature | ISO 11357-3 | 178 °C | |
| Linear coefficient of thermal expansion | MD：-- | ISO 11359-2 | 1E-04 cm/cm/°C |
| MD：-40to23°C | ISO 11359-2 | 9E-05 cm/cm/°C | |
| TD：-- | ISO 11359-2 | 1E-04 cm/cm/°C | |
| TD：-40to23°C | ISO 11359-2 | 9E-05 cm/cm/°C | |
| TD：AnnealingTemperature | ISO 11359-2 | 160 °C | |
| TD：AnnealingTime-Optional | ISO 11359-2 | 30.0 min/mm |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| burning rate | 1.00mm | ISO 3795 | <100 mm/min |
| FMVSS flammability | FMVSS302 | B | |
| Fogging-G-value | condensate | ISO 6452 | 3.5E-04 g |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Emission | VDA275 | <2.00 mg/kg | |
| Emissions of Organic Compounds | VDA277 | 10.0 µgC/g | |
| Odor | VDA270 | 3.50 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 230 kJ/m² |
| 23°C | ISO 179/1eU | 250 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| MediumDensity | 1.20 g/cm³ | ||
| melt mass-flow rate | ISO 1133 | 14 g/10min | |
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 12.0 cm3/10min |
| shrinkage rate | TD | ISO 294-4 | 1.8 % |
| MD | ISO 294-4 | 2.0 % | |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 0.90 % |
| 平衡,23°C,2.00mm,50%RH | ISO 62 | 0.20 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 43 KV/mm | |
| relative permittivity | 100Hz | IEC 60250 | 3.90 |
| 1MHz | IEC 60250 | 3.80 | |
| Dissipation Factor | 100Hz | IEC 60250 | 5E-04 |
| 1MHz | IEC 60250 | 5.5E-03 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| Surface Resistivity | IEC 60093 | >1.0E+15 ohms | |
| volume resistivity | IEC 60093 | >1.0E+15 ohms·cm |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Nominal tensile fracture strain | ISO 527-2 | 27 % | |
| flexural modulus | ISO 178 | 3150 Mpa | |
| bending strength | 3.5%应变 | ISO 178 | 85.0 Mpa |
| Tensile modulus | ISO 527-2 | 3350 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 73.5 Mpa |
| Tensile strain | 屈服 | ISO 527-2 | 13 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.