ABS CYCOLAC™ MG47F NA1000 SABIC INNOVATIVE SAUDI

553

Unit Price:US$ 2,130 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details
Material Comparison:
ABS POLYLAC® PA-707K ZHENJIANG CHIMEI

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High toughness｜Low temperature resistance｜High impact resistance｜High gloss
Application Areas:small home appliances
Color:--
Grade:--

Technical Data Sheet

Filling analysis	Test Condition	Test Method	Test Result	Test Unit
Melt viscosity	240°C, 1000 sec^-1	ASTM D3835	225	Pa·s
impact performance	Test Condition	Test Method	Test Result	Test Unit
Dart impact	23°C, Total Energy	ASTM D3763	30.0	J
Charpy Notched Impact Strength	23°C	ISO 179/1eA	26	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30°C	ISO 179/1eA	9.0	kJ/m²
flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.5 mm	UL 94	HB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	Yield, 50.0 mm Span3	ASTM D790	70.0	Mpa
bending strength	bending strength	--4,5	ISO 178	70.0	Mpa
Bending modulus	--4	ISO 178	2200	Mpa
Bending modulus	Bending modulus	50.0 mm Span3	ASTM D790	2300	Mpa
elongation	Break	ISO 527-2/50	25	%
	elongation	Break2	ASTM D638	24	%
		elongation	Yield	ISO 527-2/50	2.6	%
		elongation	elongation	Yield2	ASTM D638	2.0	%
tensile strength	Break	ISO 527-2/50	35.0	Mpa
	tensile strength	Break2	ASTM D638	33.0	Mpa
		tensile strength	Yield	ISO 527-2/50	47.0	Mpa
		tensile strength	tensile strength	Yield2	ASTM D638	44.0	Mpa
Tensile modulus	--	ISO 527-2/1	2370	Mpa
Tensile modulus	Tensile modulus	--1	ASTM D638	2270	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
drying temperature			80 to 95	°C
drying time			2.0 to 4.0	hr
Suggested maximum moisture content			0.10	%
Suggested injection volume			50 to 70	%
Temperature at the rear of the barrel			190 to 210	°C
Temperature in the middle of the barrel			205 to 225	°C
Temperature at the front of the material cylinder			215 to 240	°C
Spray nozzle temperature			220 to 260	°C
Exhaust hole depth			0.038 to 0.051	mm
Mold temperature			50 to 70	°C
Back pressure			0.300 to 0.700	Mpa
Screw speed			30 to 60	rpm
Processing (melt) temperature			220 to 260	°C
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature	--	ASTM D15258	99.0	°C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/B50	98.0	°C
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span7	ISO 75-2/Af	81.0	°C
	Hot deformation temperature	1.8 MPa, Unannealed, 3.20 mm	ASTM D648	80.0	°C
	Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed, 3.20 mm	ASTM D648	94.0	°C
Vicat softening temperature	--	ISO 306/B120	100	°C
Linear coefficient of thermal expansion	Flow : -40 to 40°C	ASTM E831	8.8E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : -40 to 40°C	ASTM E831	8.8E-5	cm/cm/°C
RTI Elec		UL 746	60.0	°C
RTI Imp		UL 746	60.0	°C
RTI		UL 746	60.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	3.20 mm，Flow	Internal Method	0.50 - 0.80	%
melt mass-flow rate	220°C/10.0 kg	ISO 1133	18	g/10 min
melt mass-flow rate	melt mass-flow rate	230°C/3.8 kg	ASTM D1238	5.6	g/10 min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Arc resistance		ASTM D495	PLC 6
Compared to the anti leakage trace index		UL 746	PLC 0
High arc combustion index		UL 746	PLC 0
High voltage arc tracing rate		UL 746	PLC 3
Hot wire ignition		UL 746	PLC 3
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R-Scale	ASTM D785	112

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Other Prices

Supplier	Unit Price
Dongguan Plastic Alliance New Materials	US$ 1810 /MT

Supplier Join

Get App

Top

ABS CYCOLAC™ MG47F NA1000 SABIC INNOVATIVE SAUDI

Material Description

Technical Data Sheet

Other Prices

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index