PC Makrolon® 1695 551022 COVESTRO BELGIUM

263

Unit Price:US$ 4,790 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
65MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility
Application Areas:Automotive Applications
Color:--
Grade:Injection grade

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
Refractive index		ISO 489	1.578
Transmittance rate	1000 μm1000 μm	ISO 13468-2	89 %

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	-30℃-30°C	ISO 179/1eU	No Break
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23℃23°C	ISO 179/1eU	No Break

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	23℃23℃	ISO 527-1-2	2400 Mpa
tensile strength	Yield，23℃Yield，23℃	ISO 527-2/50	68 Mpa
Tensile strain	Yield，23℃Yield，23℃	ISO 527-2/50	6.2 %
Nominal tensile fracture strain	23℃23℃	ISO 527-2/50	> 50 %
Bending modulus	23℃23℃3	ISO 178	2400 Mpa
bending strength	23℃	ISO 178	100 Mpa
Ball Pressure Test		ISO 2039-1	120 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8 MPa，Unannealed1.8 MPa，Unannealed	ISO 75-2/A	138 °C
Vicat softening temperature	B120B120	ISO 306/B120	158 °C
Linear coefficient of thermal expansion	TD：23~55℃TD：23 to 55℃	ISO 11359-2	0.000065 1/℃
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23~55℃MD：23 to 55℃	ISO 11359-2	0.000065 1/℃
Relative Heat Index (RTI)	电气性能电气性能	UL 746	140 °C
	Relative Heat Index (RTI)	强度机械性能强度机械性能	UL 746	140 °C
	Relative Heat Index (RTI)	Relative Heat Index (RTI)	冲击机械性能冲击机械性能	UL 746	130 °C

Physical properties	Test Condition	Test Method	Test Result
density	23°C	ISO 1183	1.18 g/cm³
melt mass-flow rate	330℃，2.16kg330℃/2.16 kg	ISO 1133	46 g/10min
Melt Volume Flow Rate (MVR)	330℃，2.16 kg330℃/2.16 kg	ISO 1133	45 cm3/10min
Shrinkage rate	TD：2.0 mmAcross Flow : 0.0787 in	ISO 294-4	0.75 %
Shrinkage rate	Shrinkage rate	MD：2.0 mmFlow : 0,0787 in	ISO 294-4	0.75 %
Water absorption rate	Saturation，23℃Saturation，23℃	ISO 62	0.3 %
Water absorption rate	Water absorption rate	Equilibrium，23℃，50% RHEquilibrium，23℃，50% RH	ISO 62	0.12 %

Electrical performance	Test Condition	Test Method	Test Result
Surface resistivity		IEC 60093	10000000000000000 ohms
Volume resistivity	23℃23℃	IEC 60093	100000000000000000 ohms·cm
Dielectric strength	23 ℃，1 mm23℃，1.00 mm	IEC 60243-1	35 KV/mm
Relative permittivity	23℃，100 Hz23°C, 100 Hz	IEC 60250	3
Relative permittivity	Relative permittivity	23℃，1 MHz23°C, 1 MHz	IEC 60250	2.9
Dissipation factor	23℃，100 Hz23°C, 100 Hz	IEC 60250	0.001
Dissipation factor	Dissipation factor	23℃，1 MHz23°C, 1 MHz	IEC 60250	0.009
Compared to the anti leakage trace index	Solution ASolution A	IEC 60112	PLC 2
Compared to the anti leakage trace index	Compared to the anti leakage trace index	Solution BSolution B	IEC 60112	PLC 4
UL flame retardant rating	1.50 mm	UL 94	HB
UL flame retardant rating	UL flame retardant rating	3.00 mm	UL 94	HB
Glow wire combustion index (GWFI)	2.0 mm2.0 mm	IEC 60695-2-12	900 °C
Extreme Oxygen Index		ISO 4589-2	26 %

Supplementary Information	Test Condition	Test Method	Test Result
Electrolytic corrosion	23℃23℃	IEC 60426	A1

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC Makrolon® 1695 551022 COVESTRO BELGIUM

Material Description

Technical Data Sheet Compare

Technical Data Sheet