impact performance	Test Condition	Test Method	Test Result	Test Unit
Impact strength of simply supported beam without notch	23℃23°C	ISO 179/1eU	130	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	-30℃-30°C	ISO 179/1eU	--	kJ/m²
Charpy Notched Impact Strength	23℃23°C	ISO 179/1eA	5	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	-30℃-30°C	ISO 179/1eA	4	kJ/m²
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
Nominal tensile fracture strain		ISO 527-2	20	%
Tensile strain	YieldYield	ISO 527-2	5	%
tensile strength	BreakBreak	ISO 527-2	50	Mpa
tensile strength	tensile strength	YieldYield	ISO 527-2	50	Mpa
Tensile modulus		ISO 527-2	2600	Mpa
Shore hardness	Shore D，15 SecShore D，15 Sec	ISO 868	--
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Linear coefficient of thermal expansion	TDTransverse	ISO 11359-2	0.00012	1/℃
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MDFlow	ISO 11359-2	0.00012	1/℃
Melting temperature		ISO 11357-3	178	°C
Continuous use temperature	---- 44	Internal Method	150	°C
Continuous use temperature	Continuous use temperature	---- 33	ISO 2578	90.0 to 120	°C
Hot deformation temperature	8.0 MPa，Unannealed1160 psi, Unannealed	ISO 75-2/C	40	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa，Unannealed264 psi, Unannealed	ISO 75-2/A	65	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
density		ISO 1183	1.44	g/cm³
Shrinkage rate	TDAcross Flow	ISO 294-4	0.9	%
Shrinkage rate	Shrinkage rate	MDFlow	ISO 294-4	0.8	%
Water absorption rate	Equilibrium，23℃，50% RHEquilibrium, 73°F, 50% RH	ISO 62	0.4	%
Water absorption rate	Water absorption rate	Saturation，23℃Saturation, 73°F	ISO 62	0.8	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index		IEC 60112		V
Dielectric strength		IEC 60243-1	--	KV/mm
Volume resistivity		IEC 60093	--	ohms·cm
Surface resistivity		IEC 60093	--	ohms
flame retardant performance	Test Condition	Test Method	Test Result	Test Unit
Flammability level		UL 94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.