PC LEXAN™  141-111L SABIC INNOVATIVE NANSHA

267
  • Unit Price:US$ 4,658 /MT
  • Packaging Specification:
    25 KG/PKG
  • Packaging Material:
    Paper bag
  • Supply Quantity:
    10.5MT
  • Delivery Terms:
    FOB
  • Port of Loading :
    China Main Port
  • Accepted Payment Methods:
    T/T
  • Shipping:
    Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View
serv********View
+86 ********View

For more details, please contact the supplier!

Material Description

  • Material Properties:Low viscosity
  • Application Areas:Automotive sector｜Household appliances
  • Color:--
  • Grade:Injection grade

Technical Data Sheet

optical performanceTest ConditionTest MethodTest Result
Refractive indexASTM D5421.586
transmissivity2540 μmASTM D100388.0 %
turbidity2540 μmASTM D10031.0 %
impact performanceTest ConditionTest MethodTest Result
Impact strength of cantilever beam gapASTM D1822577 kJ/m²
Dart impact23°CASTM D3029169 J
Dart impact23°C, Energy at PeakASTM D376363.0 J
Suspended wall beam without notch impact strength23°CASTM D48123200 J/m
flammabilityTest ConditionTest MethodTest Result
UL flame retardant rating0.71 mmUL 94HB
Extreme Oxygen IndexISO 4589-225 %
Radiation board gradeUL UnspecifiedTRUE
mechanical propertiesTest ConditionTest MethodTest Result
Taber abraser1000 Cycles, 1000 g, CS-17 WheelASTM D104410.0 mg
bending strengthYield, 50.0 mm SpanASTM D79096.0 Mpa
Bending modulus50.0 mm SpanASTM D7902340 Mpa
elongationBreakASTM D638130 %
elongationYieldASTM D6387.0 %
tensile strengthBreakASTM D63868.0 Mpa
tensile strengthYieldASTM D63862.0 Mpa
injectionTest ConditionTest MethodTest Result
drying temperature120 °C
drying time3.0 to 4.0 hr
Suggested maximum moisture content0.020 %
Suggested injection volume40 to 60 %
Temperature at the rear of the barrel270 to 295 °C
Temperature in the middle of the barrel280 to 305 °C
Temperature at the front of the material cylinder295 to 315 °C
Spray nozzle temperature290 to 310 °C
Processing (melt) temperature295 to 315 °C
Mold temperature70 to 95 °C
Back pressure0.300 to 0.700 Mpa
Screw speed40 to 70 rpm
Exhaust hole depth0.025 to 0.076 mm
thermal performanceTest ConditionTest MethodTest Result
specific heatASTM C3511250 J/kg/°C
thermal conductivityASTM C1770.27 W/m/K
RTI ElecUL 746130 °C
RTI ImpUL 746130 °C
RTIUL 746130 °C
Linear coefficient of thermal expansion-40 to 95°C，FlowASTM E8316.8E-5 cm/cm/°C
Vicat softening temperatureASTM D15255154 °C
Hot deformation temperature1.8 MPa, Unannealed, 6.40 mmASTM D648132 °C
Hot deformation temperature0.45 MPa, Unannealed, 6.40 mmASTM D648137 °C
Physical propertiesTest ConditionTest MethodTest Result
Outdoor applicabilityUL 746Cf2
Water absorption rateEquilibrium, 100°CASTM D5700.58 %
Water absorption rateEquilibrium, 23°CASTM D5700.35 %
Water absorption rate24 hrASTM D5700.15 %
Shrinkage rate3.20 mm，FlowInternal Method0.50 - 0.70 %
melt mass-flow rate300°C/1.2 kgASTM D123811 g/10 min
Specific volumeASTM D7920.830 cm³/g
Electrical performanceTest ConditionTest MethodTest Result
Volume resistivityASTM D257> 1.0E+17 ohms·cm
Dielectric strength3.20 mm, in AirASTM D14915 KV/mm
Dielectric constant60 HzASTM D1503.17
Dielectric constant50 kHzASTM D1503.17
Dielectric constant1 MHzASTM D1502.96
Dissipation factor50 HzASTM D1509.0E-4
Dissipation factor60 HzASTM D1509.0E-4
Dissipation factor1 MHzASTM D1500.010
Compared to the anti leakage trace indexUL 746PLC 2
High arc combustion indexUL 746PLC 1
High voltage arc tracing rateUL 746PLC 2
Hot wire ignitionUL 746PLC 2
hardnessTest ConditionTest MethodTest Result
Rockwell hardnessR-ScaleASTM D785118
Rockwell hardnessM-ScaleASTM D78570
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.