PC TARFLON™ LZ2510V IDEMITSU JAPAN

160

Unit Price:US$ 3,575 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant｜UV resistance
Application Areas:LCD application｜light-emitting diode
Color:--
Grade:Extrusion grade

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating	0.9mm	UL 94	V-0

mechanical properties	Test Condition	Test Method	Test Result
tensile strength	Yield	ISO 527-2	60.0 Mpa
Nominal tensile fracture strain		ISO 527-2	80 %
Charpy Notched Impact Strength		ISO 179	40 kJ/m²
bending strength		ISO 178	100 Mpa
Bending modulus		ISO 178	2300 Mpa
Elongation at Break		ISO 527-2	80 %
tensile strength	Yield	ISO 527-2	60 Mpa
bending strength		ISO 178	100 Mpa
Bending modulus		ISO 178	2300 Mpa

thermal performance	Test Condition	Test Method	Test Result
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	129 °C
Linear coefficient of thermal expansion	MD	ISO 11359-2	6.5E-05 cm/cm/°C
RTI Elec		UL 746	80.0 °C
RTI Imp		UL 746	80.0 °C
RTI Str		UL 746	80.0 °C
UL flame retardant rating	1.00 mm	UL 94	V-0
Linear coefficient of thermal expansion		ISO 11359-2	0.000065 cm/cm/℃
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	129 °C

Physical properties	Test Condition	Test Method	Test Result
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	4.00 cm3/10min
Shrinkage rate	TD:2.00mm	Internal Method	0.50-0.70 %
Shrinkage rate	Shrinkage rate	MD:2.00mm	Internal Method	0.50-0.70 %
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.23 %
Water absorption rate	Water absorption rate	Equilibrium,23℃, 50% RH	ISO 62	0.23 %
Shrinkage rate	MD: 2.00 mm	Internal Method	0.5-0.7 %
Shrinkage rate	Shrinkage rate	TD	Internal Method	0.5-0.7 %
Melt Volume Flow Rate (MVR)	MVR	ISO 1133	3 cm3/10min

Electrical performance	Test Condition	Test Method	Test Result
Compared to the anti leakage trace index	CTI	UL 746	PLC 3

hardness	Test Condition	Test Method	Test Result
Rockwell hardness	M-Sale	ISO 2039-2	50
Rockwell hardness	Rockwell hardness	R-Sale	ISO 2039-2	120

Supplementary Information	Test Condition	Test Method	Test Result
ISO Shortcut			>PC<

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC TARFLON™ LZ2510V IDEMITSU JAPAN

Material Description

Technical Data Sheet Compare

Technical Data Sheet