PA66 TECHNYL® A218G1V30 BK SOLVAY FRANCE
192
- Unit Price:US$ 3,689 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:40MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | ISO 62 | 0.80 % | |
| ISO 62 | 5.3 % | ||
| ISO 62 | 1.7 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB | |
| Burning wire flammability index | IEC 60695-2-12 | 650 °C | |
| Limiting Oxygen Index | ISO 4589-2 | 23 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A | 10000 Mpa | |
| tensile strength | ISO 527-2/1A | 190 Mpa | |
| Tensile strain | ISO 527-2 | 3.2 % | |
| Flexural modulus | ASTM D790 | 9700 Mpa | |
| ISO 178 | 9000 Mpa | ||
| bending strength | ASTM D790 | 275 Mpa | |
| ISO 178 | 290 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179/1eU | 85 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | 6.0E+15 ohms | |
| Volume resistivity | IEC 60093 | 1.0E+15 ohms·cm | |
| dielectric strength | IEC 60243-1 | 34 KV/mm | |
| Dissipation Factor | IEC 60250 | 0.010 | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 1 |
| injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| drying temperature | 80 °C | ||
| Suggested maximum moisture content | 0.15 % | ||
| Temperature at the rear of the barrel | 270 to 280 °C | ||
| Temperature in the middle of the barrel | 275 to 285 °C | ||
| Temperature at the front of the material cylinder | 280 to 290 °C | ||
| Temperature | 70 to 100 °C |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/Af | 250 °C | |
| melting temperature | ISO 11357-3 | 263 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.