PC/ABS INFINO® NH-1045 BK Samsung Cheil South Korea

282

Unit Price:US$ 2,862 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:Flame retardant
Application Areas:sporting facilities
Color:--
Grade:High liquidity level

Technical Data Sheet

flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	1.530mm	UL 94	V-0
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	--5	ISO 178	93.0	Mpa
bending strength	bending strength	--4	ASTM D790	91.0	Mpa
Bending modulus	--5	ISO 178	2600	Mpa
Bending modulus	Bending modulus	--4	ASTM D790	2600	Mpa
elongation	Break	ISO 527-2/50	50	%
elongation	elongation	Break3	ASTM D638	50	%
tensile strength	Break	ISO 527-2/50	45.0	Mpa
	tensile strength	Break3	ASTM D638	44.0	Mpa
		tensile strength	Yield	ISO 527-2/50	63.0	Mpa
		tensile strength	tensile strength	Yield3	ASTM D638	62.0	Mpa
Tensile modulus	--	ISO 527-2/50	2500	Mpa
Tensile modulus	Tensile modulus	--3	ASTM D638	2500	Mpa
injection	Test Condition	Test Method	Test Result	Test Unit
Hot air dryer			80	°C
Vacuum drying machine			80	°C
Hot air dryer			4.0	hr
Vacuum drying machine			4.0	hr
Suggested maximum moisture content			0.020	%
Temperature at the rear of the barrel			230 to 270	°C
Temperature in the middle of the barrel			240 to 280	°C
Temperature at the front of the material cylinder			250 to 290	°C
Spray nozzle temperature			250 to 290	°C
Mold temperature			60 to 80	°C
Injection pressure			98.1	Mpa
Back pressure			0.981 to 2.94	Mpa
Screw speed			50 to 200	rpm
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Vicat softening temperature		ISO 306/B50	95.0	°C
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm	ISO 75-2/A	78.0	°C
	Hot deformation temperature	1.8 MPa, Unannealed, 6.40 mm	ASTM D648	80.0	°C
		Hot deformation temperature	0.45 MPa, Unannealed, 4.00 mm	ISO 75-2/B	88.0	°C
		Hot deformation temperature	Hot deformation temperature	0.45 MPa, Unannealed, 6.40 mm	ASTM D648	88.0	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Shrinkage rate	Flow : 2.00 mm	ISO 294-4	0.40 - 0.70	%
	Shrinkage rate	横向Flow : 2.00 mm	ISO 294-4	0.40 - 0.70	%
		Shrinkage rate	Across FlowFlow : 3.20 mm	ASTM D955	0.40 - 0.70	%
		Shrinkage rate	Shrinkage rate	Flow : 3.20 mm	ASTM D955	0.40 - 0.70	%
melt mass-flow rate	220°C/10.0 kg	ASTM D1238	55	g/10 min
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R -Sale	ISO 2039-2	116
Rockwell hardness	Rockwell hardness	R-Scale	ASTM D785	116

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Supplier Join

Get App

Top

PC/ABS INFINO® NH-1045 BK Samsung Cheil South Korea

Material Description

Technical Data Sheet

Sourcing & Prices

Selling & Verification

Explore Materials

Price Index