PC Makrolon® 2407 021533 COVESTRO SHANGHAI
333
- Unit Price:US$ 3,584 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:10MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Low viscosity｜UV resistance｜High mobility｜Thermal stability｜Good demolding performance
- Application Areas:Industrial applications｜Electrical field｜Electronic field｜Automotive sector｜currency｜currency
- Color:--
- Grade:High liquidity level
Technical Data Sheet
Compare
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ball-indentation hardness | ISO 2039-1 | 116 Mpa |
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | ISO 75-2/Bf | 136 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 6.5E-05 cm/cm/°C | |
| Heat Deflection Temperature | ISO 75-2/Af | 124 °C | |
| vicat | ISO 306/B50 | 143 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 6.5E-05 cm/cm/°C |
| optical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| refractive index | ISO 489 | 1.58 °C | |
| transmittance | ISO 13468-2 | 89.0 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Elongation at break | ISO 527-2 | >50 % | |
| Tensile modulus | ISO 527-2 | 2400 Mpa | |
| tensile strength | ISO 527-2 | 66.0 Mpa | |
| Tensile creep modulus | ISO 899-1 | 2200 Mpa | |
| ISO 899-1 | 1900 Mpa | ||
| bending strength | ISO 178 | 98.0 Mpa | |
| flexural modulus | ISO 178 | 2350 Mpa | |
| Charpy Notched Impact Strength | ISO 179/1eA | 65 kJ/m² | |
| ISO 179/1eA | 14 kJ/m² | ||
| Impact strength of cantilever beam gap | ISO 180/1A | 75 kJ/m² | |
| ISO 180/1A | 12 kJ/m² |
| flame retardant performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Limiting Oxygen Index | ISO 4589-2 | 27 % | |
| UL flame retardant rating | UL -94 | V-2 1.50mm | |
| UL -94 | V-2 2.60mm | ||
| UL -94 | V-2 0.75mm | ||
| UL -94 | HB 3.00mm | ||
| UL -94 | HB 2.70mm | ||
| UL -94 | HB 6.00mm |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Water absorption rate | ISO 62 | 0.12 % | |
| melt mass-flow rate | ISO 1133 | 19.0 cm3/10min | |
| shrinkage rate | ISO 294-4 | 0.70 % | |
| Water absorption rate | ISO 62 | 0.30 % | |
| density | ISO 1183 | 1.2 g/cm³ | |
| shrinkage rate | ISO 294-4 | 0.65 % |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dissipation Factor | IEC 60250 | 5E-04 100HZ | |
| dielectric constant | IEC 60250 | 3.00 1MHz | |
| dielectric strength | IEC 60243-1 | 25 KV/mm | |
| Surface Resistivity | IEC 60093 | 1E+16 Ω.cm | |
| volume resistivity | IEC 60093 | 1E+15 Ω.cm | |
| Dissipation Factor | IEC 60112 | 250 V | |
| IEC 60250 | 9E-03 1MHz |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.