Other performance	Test Condition	Test Method	Test Result	Test Unit
tensile strength		ISO 527	36	Mpa
Basic Performance	Test Condition	Test Method	Test Result	Test Unit
Shore hardness	Shore D	ISO 868	63
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
tensile strength		ISO 527	36	Mpa
Elongation at Break		ISO 527	460	%
Flexural elasticity		ISO 178	300	Mpa
Impact strength of cantilever beam gap		ISO 179/IeA	PARTIAL BREAK	kJ/㎡
Volume resistivity		IEC 60093	7.0E 13	Ohm cm
Volume resistivity	Volume resistivity		IEC 60093	3.0E 13	Ohm
Dielectric strength		IEC 60243	17	KV/mm
Shore hardness	Shore D	ISO 868	63
tensile strength	Yield	ISO 527-2	40.0	Mpa
Tensile strain	Break	ISO 527-2	460	%
Bending modulus		ISO 178	350	Mpa
Charpy Notched Impact Strength		ISO 179/1eA	无断裂
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Melting temperature		ISO 3146C	211	°C
melt mass-flow rate	2.16kg at 230℃	ISO 1133	8	g/10 min
Melting temperature		ISO 3146	212	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	24hr	ISO 62	0.5	%
Shrinkage rate		ISO 294-4	1.7	%
melt mass-flow rate	230℃/2.16 kg	ISO 1133	20	g/10 min
Shrinkage rate		ISO 294-4	1.3	%
Water absorption rate	23℃, 24 hr	ISO 62	0.30	%
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Surface resistivity		IEC 60093	2.8E+15	Ohm
Volume resistivity		IEC 60093	6.3E+13	ohm·cm
Dielectric strength	2.00 mm	IEC 60243-1	17	KV/mm

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.