PC EMERGE™ 8130-6 IC1300102E STYRON TAIWAN
94
- Unit Price:US$ 2,537 /MT
- Packaging Specification:
- Supply Quantity:31MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Flame retardant grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| RTI Elec | UL 746 | 130 °C | |
| RTI Imp | UL 746 | 115 °C | |
| Heat Deflection Temperature | 0.45MPa,未退火,6.40mm | ASTM D648 | 137 °C |
| RTI Str | UL 746 | 130 °C | |
| Heat Deflection Temperature | 1.8MPa,未退火,6.40mm | ASTM D648 | 127 °C |
| vicat | ASTM D1525 | 151 °C | |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 6.5E-05 cm/cm/°C |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.9mm | 内部方法 | V-1 |
| 0.9mm | 内部方法 | V-0 | |
| 1.0mm | 内部方法 | V-0 | |
| 2.0mm | 内部方法 | 5VB | |
| 3.0mm | 内部方法 | 5VA |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Dart impact | ASTM D3763 | 62.1 J | |
| Impact strength of cantilever beam gap | ASTM D1822 | 630 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 10 g/10min |
| shrinkage rate | MD | ASTM D955 | 0.50-0.70 % |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.15 % |
| Outdoor applicability | UL 746C | f1 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| arc resistance | ASTM D495 | PLC7 | |
| Compared to the Leakage Tracking Index (CTI) | CTI | UL 746 | PLC 2 |
| High arc combustion index (HAI) | 0.9mm | UL 746 | PLC 2 |
| 1.0to3.0mm | UL 746 | PLC 1 | |
| High Voltage Arc Traceability Rate (HVTR) | PLC | UL 746 | PLC 1 |
| Hot wire ignition (HWI) | 0.9to3.0mm | UL 746 | PLC 2 |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 120 % |
| flexural modulus | ASTM D790 | 2330 Mpa | |
| bending strength | ASTM D790 | 97.9 Mpa | |
| Tensile modulus | ASTM D638 | 2380 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 61.4 Mpa |
| 屈服 | ISO 527-2/50 | 61.0 Mpa | |
| 断裂 | ASTM D638 | 58.6 Mpa | |
| 断裂 | ISO 527-2/50 | 59.0 Mpa | |
| elongation | 屈服 | ASTM D638 | 6.0 % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.