thermal performance	Test Condition	Test Method	Test Result
Heat Deflection Temperature	1.8MPa,未退火,64.0mm跨距	ISO 75-2/Af	118 °C
vicat	--	ISO 306/B50	135 °C
vicat	vicat	--	ISO 306/B120	137 °C
Linear coefficient of thermal expansion	MD：-40到40°C	ISO 11359-2	6E-05 cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：-40到40°C	ISO 11359-2	7E-05 cm/cm/°C

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap	-30°C	ISO 180/1A	10 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180/1A	30 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	35 kJ/m²

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	饱和,23°C	ISO 62	0.40 %
Water absorption rate	Water absorption rate	平衡,23°C,50%RH	ISO 62	0.10 %
Melt volume flow rate	265°C/5.0kg	ISO 1133	10.0 cm3/10min
shrinkage rate	MD：3.20mm	内部方法	0.40-0.60 %

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO 527-2/1	3200 Mpa
tensile strength	屈服	ISO 527-2/5	55.0 Mpa
tensile strength	tensile strength	断裂	ISO 527-2/5	58.0 Mpa
Tensile strain	屈服	ISO 527-2/5	4.2 %
Tensile strain	Tensile strain	断裂	ISO 527-2/5	100 %
flexural modulus		ISO 178	3100 Mpa
bending strength		ISO 178	95.0 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.