POM CELCON® UV90Z CELANESE USA
202
- Unit Price:US$ 3,039 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:97.3MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:Weather resistance｜High mobility｜UV resistance｜Automotive interior parts
- Application Areas:Automotive Applications｜pipeline
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat Deflection Temperature | 0.45MPa,未退火 | ISO 75-2/B | 155 °C |
| 1.8MPa,未退火 | ASTM D648 | 110 °C | |
| 1.8MPa,未退火 | ISO 75-2/A | 91.0 °C | |
| melting temperature | ASTM D3418 | 165 °C | |
| ISO 11357-3 | 165 °C | ||
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| TD | ISO 11359-2 | 1.2E-04 cm/cm/°C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 6.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 100 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 5.7 kJ/m² |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| shrinkage rate | TD | ISO 294-4 | 1.7 % |
| MD | ISO 294-4 | 1.9 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.75 % |
| 平衡,23°C,50%RH | ISO 62 | 0.20 % | |
| density | ASTM D792 | 1.41 g/cm³ | |
| ISO 1183 | 1.41 g/cm³ | ||
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 8.00 cm3/10min |
| shrinkage rate | MD | ASTM D955 | 2.2 % |
| TD | ASTM D955 | 1.8 % |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A/1 | 2700 Mpa | |
| tensile strength | 屈服,23°C | ASTM D638 | 60.7 Mpa |
| 屈服 | ISO 527-2/1A/50 | 64.0 Mpa | |
| Tensile strain | 屈服 | ISO 527-2/1A/50 | 9.0 % |
| flexural modulus | 23°C | ISO 178 | 2470 Mpa |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.