PEI

PEI ULTEM™ AUT200-1000 SABIC INNOVATIVE SPAIN

272

Unit Price:US$ 17,818 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
16MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High mobility｜High transparency｜high definition
Application Areas:Electrical appliances｜Automotive Applications
Color:--
Grade:--

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	NoBreak
Impact strength of cantilever beam gap	23°C	ISO 180/1A	5.0 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	-30°C	ISO 180/1A	5.0 kJ/m²
Charpy Notched Impact Strength	23°C	ISO 179/1eA	3.0 kJ/m²
Suspended wall beam without notch impact strength	23°C	ISO 180/1U	NoBreak
Dart impact	23°C,TotalEnergy	ASTM D3763	33.0 J

mechanical properties	Test Condition	Test Method	Test Result
bending strength	Yield,50.0mmSpan	ASTM D790	165 Mpa
bending strength	bending strength		ISO 178	160 Mpa
Bending modulus		ISO 178	3300 Mpa
Tensile strain	Break	ISO 527-2/5	60 %
elongation	Break	ASTM D638	60 %
Tensile strain	Yield	ISO 527-2/5	6.0 %
elongation	Yield	ASTM D638	7.0 %
tensile strength	Break	ISO 527-2/5	85.0 Mpa
	tensile strength	Break	ASTM D638	105 Mpa
		tensile strength	Yield	ISO 527-2/5	105 Mpa
		tensile strength	tensile strength	Yield	ASTM D638	110 Mpa
Tensile modulus		ISO 527-2/1	3200 Mpa
Tensile modulus	Tensile modulus		ASTM D638	3590 Mpa
Bending modulus	50.0mmSpan	ASTM D790	3520 Mpa

thermal performance	Test Condition	Test Method	Test Result
Linear coefficient of thermal expansion	MD：23to150°C	ISO 11359-2	5E-05 cm/cm/°C
	Linear coefficient of thermal expansion	TD：-40to150°C	ASTME831	5.5E-05 cm/cm/°C
		Linear coefficient of thermal expansion	MD：-40to150°C	ASTME831	5.5E-05 cm/cm/°C
		Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD：23to150°C	ISO 11359-2	5E-05 cm/cm/°C
Hot deformation temperature	0.45MPa,Unannealed,3.20mm	ASTM D648	205 °C
	Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	197 °C
		Hot deformation temperature	1.8MPa,Unannealed,6.40mm	ASTM D648	199 °C
			Hot deformation temperature	1.8MPa,Unannealed,100mmSpan9	ISO 75-2/Ae	190 °C
			Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed,64.0mmSpan10	ISO 75-2/Af	193 °C
Vicat softening temperature		ASTM D152511	219 °C
	Vicat softening temperature	--	ISO 306/B50	211 °C
	Vicat softening temperature	Vicat softening temperature	--	ISO 306/B120	212 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.70 %
Water absorption rate	Water absorption rate	Saturation,23°C	ISO 62	1.3 %
Shrinkage rate	MD：3.20mm	Internal Method	0.50-0.70 %
Melt Volume Flow Rate (MVR)	360°C/5.0kg	ISO 1133	25.0 cm3/10min
melt mass-flow rate	337°C/6.6kg	ASTM D1238	18 g/10min

Supplementary Information	Test Condition	Test Method	Test Result
Metallic haze	起始	Internal Method	204 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PEI ULTEM™ AUT200-1000 SABIC INNOVATIVE SPAIN

Material Description

Technical Data Sheet Compare

Technical Data Sheet