flammability	Test Condition	Test Method	Test Result	Test Unit
UL flame retardant rating	0.8mm	UL 94	HB
	UL flame retardant rating	0.8mm	UL 94	V-1
		UL flame retardant rating	1.5mm	UL 94	V-0
		UL flame retardant rating	UL flame retardant rating	2.0mm	UL 94	5VB
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength		ISO 178	90.0	Mpa
tensile strength	Yield	ISO 527-2	60.0	Mpa
Nominal tensile fracture strain		ISO 527-2	100	%
Bending modulus		ISO 178	2100	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	138	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	123	°C
Linear coefficient of thermal expansion	MD	ISO 11359-2	8E-05	cm/cm/°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Melt Volume Flow Rate (MVR)	300°C/1.2kg	ISO 1133	11.0	cm3/10min
Spiral flow length		Internal Method	25.0	CM
Shrinkage rate	TD:2.00mm	Internal Method	0.60-0.80	%
Shrinkage rate	Shrinkage rate	MD:2.00mm	Internal Method	0.60-0.80	%
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.20	%
Outdoor applicability	Black	UL 746C	f1
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Compared to the anti leakage trace index	CTI	UL 746	PLC 3
Supplementary Information	Test Condition	Test Method	Test Result	Test Unit
ISO Shortcut			>PC<

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.