PPS Torelina® A604 TORAY JAPAN
387
- Unit Price:US$ 7,075 /MT
- Packaging Specification:25 KG/PKG
- Packaging Material:Paper bag
- Supply Quantity:153MT
- Delivery Terms:FOB
- Port of Loading :China Main Port
- Accepted Payment Methods:T/T
- Shipping:Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 ********View
serv********View
For more details, please contact the supplier!
Material Description
- Material Properties:High temperature resistance｜Glass fiber reinforced｜Flame retardant
- Application Areas:sporting goods｜Automotive sector｜Electronic field｜Electrical field
- Color:--
- Grade:Injection grade
Material Certification
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | 内部方法 | 0.80 % | |
| 内部方法 | 0.20 % | ||
| Water absorption rate | ISO 62 | 0.020 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 122 |
| other | Test Condition | Test Method | Test Result |
|---|---|---|---|
| characteristic | 40%加纤.增强.高韧性 | ||
| Color | 米色.黑色 |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|---|---|---|
| BarFlowLength | 内部方法 | 120 mm |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 12 kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 60 kg·cm/cm(J/M)ft·lb/in | ||
| elongation at break | ASTM D638/ISO 527 | 2 % | |
| tensile strength | ASTM D638/ISO 527 | 205 kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 122 | |
| Flexural modulus | ASTM D790/ISO 178 | 14.5 kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 300 kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ISO 527-2 | 205 Mpa | |
| Tensile strain | ISO 527-2 | 2.0 % | |
| Flexural modulus | ISO 178 | 14500 Mpa | |
| bending strength | ISO 178 | 300 Mpa | |
| shear strength | JISK7214 | 80.0 Mpa | |
| coefficient of friction | 0.24 | ||
| Taber abraser | ISO 9352 | 50.0 mg |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 60 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| dielectric constant | ASTM D150/IEC 60250 | 3.6 | |
| Volume resistivity | ASTM D257/IEC 60093 | 1014 Ω.cm | |
| IEC 60093 | 1E+16 ohms·cm | ||
| dielectric strength | IEC 60243-1 | 24 KV/mm | |
| dielectric constant | IEC 60250 | 3.60 | |
| Dissipation Factor | IEC 60250 | 2E-03 |
| Physical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.66 | |
| Shrinkage rate | ASTM D955 | 0.2 % | |
| Water absorption rate | ASTM D570/ISO 62 | 0.02 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-0 | |
| Heat distortion temperature | ASTM D648/ISO 75 | >260 ℃（℉） | |
| melting temperature | 278 ℃（℉） | ||
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 2.3 mm/mm.℃ | |
| Heat distortion temperature | ISO 75-2/A | 260 °C | |
| melting temperature | ISO 11357-3 | 278 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 2.3E-05 cm/cm/°C | |
| ISO 11359-2 | 3.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.