PC Makrolon® 3208 550111 COVESTRO BELGIUM

289

Unit Price:US$ 6,095 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
45MT
Delivery Terms:
FOB
Port of Loading :
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:High impact resistance｜high molecular weight｜Drinking water contact
Application Areas:building materials｜Casters｜Transportation equipment
Color:--
Grade:--

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result
Refractive index		ISO 489	1.587
Transmittance rate	1000 μm	ISO 13468-2	89 %
	Transmittance rate	2000 μm	ISO 13468-2	89 %
		Transmittance rate	3000 μm	ISO 13468-2	88 %
		Transmittance rate	Transmittance rate	4000 μm	ISO 13468-2	87 %
turbidity	3000 μm	ISO 14782	< 0.80 %

impact performance	Test Condition	Test Method	Test Result
Charpy Notched Impact Strength	-30℃，Complete Break-22°F, Complete Break	ISO 7391	18 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23℃，Partial Break73°F, Partial Break	ISO 7391	80 kJ/m²
Impact strength of simply supported beam without notch	-60℃-60°C	ISO 179/1eU	No Break
	Impact strength of simply supported beam without notch	-30℃-30°C	ISO 179/1eU	No Break
	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23℃23°C	ISO 179/1eU	No Break
Impact strength of cantilever beam gap	-30℃，Complete Break-22°F, Complete Break	ISO 7391	20 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23℃，Partial Break73°F, Partial Break	ISO 7391	75 kJ/m²
Multi axis Instrumented Impact Energy	-30℃-30°C	ISO 6603-2	75 J
Multi axis Instrumented Impact Energy	Multi axis Instrumented Impact Energy	23℃23°C	ISO 6603-2	65 J
Multi axis Instrumented Peak Impact Force	-30℃-30°C	ISO 6603-2	6700 N
Multi axis Instrumented Peak Impact Force	Multi axis Instrumented Peak Impact Force	23℃23°C	ISO 6603-2	5800 N

mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus	23℃	ISO 527-1-2	2350 Mpa
tensile strength	Break，23℃	ISO 527-2/50	75 Mpa
tensile strength	tensile strength	Yield，23℃	ISO 527-2/50	65 Mpa
Tensile strain	Break，23℃	ISO 527-2/50	120 %
Tensile strain	Tensile strain	Yield，23℃	ISO 527-2/50	6.3 %
Nominal tensile fracture strain	23℃	ISO 527-2/50	> 50 %
Tensile Creep Modulus（1 hr）Tensile Creep Modulus (1 hr)		ISO 899-1	2200 Mpa
Tensile creep modulus	1000 hr	ISO 899-1	1900 Mpa
Bending modulus	23℃23℃4	ISO 178	2350 Mpa
bending strength	3.50% Strain，23℃3.5% Strain, 23°C	ISO 178	72 Mpa
bending strength	bending strength	23℃23°C	ISO 178	95 Mpa
Bending strain	23°C	ISO 178	7.2 %
Ball Pressure Test		ISO 2039-1	111 Mpa

thermal performance	Test Condition	Test Method	Test Result
Glass transition temperature		ISO 11357-2	150 °C
Vicat softening temperature	B50--	ISO 306	150 °C
Vicat softening temperature	Vicat softening temperature	B120--	ISO 306/B120	151 °C
Ball indentation test	141℃141℃	IEC 60695-10-2	Pass
Linear coefficient of thermal expansion	TD：23~55℃	ISO 11359-2	0.000065 1/℃
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	MD：23~55℃	ISO 11359-2	0.000065 1/℃
thermal conductivity	23℃23℃9	ISO 8302	0.2 W/m/K

Physical properties	Test Condition	Test Method	Test Result
density	23°C	ISO 1183	1.2 g/cm³
Apparent density		ISO 60	0.66 g/cm³
melt mass-flow rate	300℃，1.20kg300℃/1.2 kg	ISO 1133	5.5 g/10min
Melt Volume Flow Rate (MVR)	300℃，1.2 kg300℃/1.2 kg	ISO 1133	5 cm3/10min
Shrinkage rate	TDAcross Flow	ISO 2577	0.60 - 0.80 %
	Shrinkage rate	MDFlow	ISO 2577	0.60 - 0.80 %
		Shrinkage rate	TD：2.0 mmAcross Flow : 0.0787 in 33	ISO 294-4	0.75 %
		Shrinkage rate	Shrinkage rate	MD：2.0 mmFlow : 0.0787 in 33	ISO 294-4	0.7 %
Water absorption rate	Saturation，23℃Saturation，23℃	ISO 62	0.3 %
Water absorption rate	Water absorption rate	Equilibrium，23℃，50% RHEquilibrium，23℃，50% RH	ISO 62	0.12 %

flame retardant performance	Test Condition	Test Method	Test Result
Flash Ignition TemperatureFlash Ignition Temperature		ASTM D1929	480 °C
auto-ignition temperature		ASTM D1929	550 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App

Top

PC Makrolon® 3208 550111 COVESTRO BELGIUM

Material Description

Technical Data Sheet Compare

Technical Data Sheet