PC 8000-05 LG CHEM KOREA

351

Unit Price:US$ 3,460 /MT
Packaging Specification:
25 KG/PKG
Packaging Material:
Paper bag
Supply Quantity:
20MT
Delivery Terms:
FOB
Port of Loading :
Guangzhou port, China
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 ********View

serv********View

+86 ********View

For more details, please contact the supplier!

Material Description

Material Properties:high strength｜High rigidity
Application Areas:Lighting applications｜Electrical applications
Color:--
Grade:Injection grade

Technical Data Sheet

optical performance	Test Condition	Test Method	Test Result	Test Unit
transmissivity	3000 μm	ASTM D1003	> 88.0	%
transmissivity	transmissivity	3000 μm	ISO 13468-1	> 88.0	%
turbidity	3000 μm	ASTM D1003	< 1.0	%
turbidity	turbidity	3000 μm	ISO 14782	< 1.0	%
impact performance	Test Condition	Test Method	Test Result	Test Unit
Suspended wall beam without notch impact strength	23°C	ASTM D256	无断裂
mechanical properties	Test Condition	Test Method	Test Result	Test Unit
bending strength	--	ISO 178	82.0	Mpa
bending strength	bending strength	--	ASTM D790	86.0	Mpa
Bending modulus	--	ISO 178	1940	Mpa
Bending modulus	Bending modulus	--	ASTM D790	2030	Mpa
elongation	Break	ISO 527-2	110	%
	elongation	Break	ASTM D638	120	%
	elongation	elongation	Yield	ASTM D638	6.0	%
tensile strength	Break	ISO 527-2	64.0	Mpa
	tensile strength	Break	ASTM D638	68.0	Mpa
		tensile strength	Yield, 23°C	ISO 527-2/50	57.0	Mpa
		tensile strength	tensile strength	Yield, 23°C2	ASTM D638	58.0	Mpa
Tensile modulus	--	ISO 527-2	2390	Mpa
Tensile modulus	Tensile modulus	--	ASTM D638	2180	Mpa
thermal performance	Test Condition	Test Method	Test Result	Test Unit
Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	115	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Annealed, 4.00 mm	ASTM D648	130	°C
Vicat softening temperature		ISO 306/B120	138	°C
Linear coefficient of thermal expansion	-40 to 82°C，Flow	ASTM D696	7.0E-5	cm/cm/°C
Hot deformation temperature	1.8 MPa, Unannealed, 4.00 mm	ASTM D648	118	°C
Hot deformation temperature	Hot deformation temperature	0.45 MPa, Annealed, 4.00 mm	ASTM D648	132	°C
Physical properties	Test Condition	Test Method	Test Result	Test Unit
Water absorption rate	Equilibrium, 23°C, 50% RH	ASTM D570	0.20	%
Water absorption rate	Water absorption rate	24 hr, 23°C	ASTM D570	0.12	%
Shrinkage rate	Flow	ASTM D955	0.50 - 0.70	%
melt mass-flow rate	300°C/1.2 kg	ASTM D1238	3.5	g/10 min
Electrical performance	Test Condition	Test Method	Test Result	Test Unit
Volume resistivity	23°C	ASTM D257	1.0E+15	ohms·cm
hardness	Test Condition	Test Method	Test Result	Test Unit
Rockwell hardness	R -Sale	ISO 2039-2	120
	Rockwell hardness	M -Sale	ISO 2039-2	50
		Rockwell hardness	R-Scale	ASTM D785	120
		Rockwell hardness	Rockwell hardness	M-Scale	ASTM D785	50

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.